Abstract:The vulcanization reaction of ethylene vinyl acetate copolymer (EVM) rubber is fast, resulting in poor processing safety. EVM is often filled with flame-retardant fillers as insulating or sheathing material for wires and cables. Herein, the effects of flame-retardant magnesium hydroxide (Mg(OH) 2 ), aluminum hydroxide (Al(OH) 3 ) and of the traditional reinforcing fillers carbon black (CB) and silicon dioxide (SiO 2 ) on the vulcanization kinetics of EVM were investigated. The vulcanization characteristics showed that the scorch time (T 10 ) of the unfilled EVM (KB), SiO 2 /EVM, Mg(OH) 2 /EVM, and Al(OH) 3 /EVM composites was about 1.75 min. T 10 of the CB/EVM composite was 2.22 min. Compared with KB, the activation energy (E a ) increased by about 15 kJ/mol for CB/EVM composites and by about 5 kJ/mol for SiO 2 /EVM, Mg(OH) 2 /EVM and Al(OH) 3 /EVM composites. The results indicate that CB delays the vulcanization time of EVM rubber, slows down the rate of vulcanization reaction and improves the safety of vulcanization. The addition of SiO 2 , Mg(OH) 2 and Al(OH) 3 has little effect on the vulcanization reaction. The mechanical properties show that CB/EVM is more uniformly vulcanized and has the best mechanical properties with a tensile strength of 17.61 MPa and elongation at break of 404.58 %. Mg(OH) 2 /EVM and Al(OH) 3 /EVM samples have prominent vulcanization non-uniformity resulting in poor mechanical properties.

Preparation and Characterization of Magnesium HydroxideGround Calcium Carbonate Composite Flame Retardant Fillers

Preparation of Magnesium Hydroxide Flame Retardant from Hydromagnesite and Enhance the Flame Retardant Performance of EVA

Preparation and characterization of Mg(OH)2 nanoparticles and flame-retardant property of its nanocomposites with EVA

Preparation and Application of Flame - Retard Type Magnesium Hydroxide

Preparation and characterization of ethylene–vinyl acetate copolymer (EVA)–magnesium hydroxide (MH)–hexaphenoxycyclotriphosphazene (HPCTP) composite flame-retardant materials

Effect of Particle Size on Flame Retardancy of Mg(OH)2‐filled Ethylene Vinyl Acetate Copolymer Composites

Rheological and Aesthetical Properties of Polyolefin Composites for Flame Retardant Cables with High Loading of Mineral Fillers

Influence of Maleic Anhydride Grafted Ethylene-Vinyl Acetate Copolymer as a Compatibilizer on Combustion and Thermal Stability Properties of Magnesium Hydroxide Flame-Retardant Ethylene Propylene Diene Terpolymer Composites

Synthesis of magnesium hydroxide flame retardant based on microcrystalline magnesite and its application in epoxy resin

Polyolefin Composites Filled with Magnesium Hydroxide

Flame Retardancy of EVA Filled by Mg(OH)2 and Al(OH)3

A Facile Approach to Prepare Anhydrous MgCO 3 and Its Effect on the Mechanical and Flame Retardant Properties of PVC Composites

Vulcanization kinetics and mechanical properties of filled ethylene-vinyl acetate copolymer rubber composites

Mechanical, thermal and flame retardant properties of magnesium hydroxide filled poly(vinyl chloride) composites: The effect of filler shape

Effect of Polyolefin Elastomers’ Characteristics and Natural Magnesium Hydroxide Content on the Properties of Halogen-Free Flame-Retardant Polyolefin Composites

Influence of Fe-MMT on the fire retarding behavior and mechanical property of (ethylene-vinyl acetate copolymer/magnesium hydroxide) composite

Enhancement of thermal stability and flame retardancy of ethylene vinyl acetate/magnesium hydroxide composite by carbon black

Effect of Stearic Acid and Epoxy Silane on the Structure and Flame‐retardant Properties of Magnesium Hydroxide/ethylene Vinyl Acetate Copolymer/very Low Density Polyethylene Composites

Synergistic effect of modified anhydrous magnesium carbonate and hexaphenoxycyclotriphosphazene on flame retardancy of ethylene-vinyl acetate copolymer

Study of Non-halogen Flame Retardant Polyolefin Elastomer

FMagnesium hydroxide-based flame-retardant fillers for polymer materials and the effect of particle size on the dehydration process at high temperatures