Preparation of Chitosan Coated Lysozyme-Poly(d,l-lacticco-glycolic Acid) Cationic Nanospheres

Yan Xiao

2010-01-01

Abstract:Biodegradable poly(D,L-lactic-co-glycolic acid)(PLGA) was activated by N,N′-dicyclohexylcarbodiimide followed by chemical bonding to lysozyme.The resulting material was directly incorporated into nanospheres by an oil-in-water(O/W) single emulsion solvent evaporation method with its cationic surface modified by chitosan(CHS).The various conditions were optimized.The results showed that the diameter of the nanospheres can be controlled within a range of(450±50)nm,and the ζ potential of the nanospheres can be as high as 42.5mV when the pH was 4.2.The optimized conditions were as follows: ρ(CHS) of 3mg/mL,ρ(PLGA) of 5mg/mL,and a content ratio of lysozyme to PLGA of 0.2/1.The nanospheres obtained under the optimized conditions showed a loading efficiency and encapsulation efficiency of 14.7% and 87.8% respectively,while the encapsulation efficiency was only 41.0% for nanospheres prepared by a W/O/W method,with all other conditions the same as for the preparation using the O/W method.SEM micrographs showed that when lysozyme-PLGA nanospheres were modified with CHS,the regular spherical shape was retained.The material displayed a sustained release rate of 70% after 20 days of release and a regular sustained release curve,as compared with a release rate of 90% after 10 days for nanospheres prepared previously by W/O/W methods,demonstrating the superior sustained release properties of the new material.