Abstract:Tungsten production primarily relies on scheelite, a secondary resource due to its complex ore composition and lower grade compared to high-grade wolframite. Synthetic scheelite gains significance for its low impurity content and accessibility in ongoing laboratory-based investigations. Recent advancements offer a feasible environment-friendly leaching method using a mixed solution of H 2 SO 4 and H 2 O 2 under normal pressure and moderate temperatures. However, comprehensive research on this novel method is lacking, emphasising the need for collaborative exploration and operational optimisation. The present work is to provide insights and improvements in reagent usage to promote economic and environmental sustainability. A detailed investigation into the thermal decomposition process was also conducted without compromising leaching efficiency. The findings suggest the potential for eco-friendly lixivium recycling with reduced levels of chemicals, decreasing operational costs. Notably, optimising the thermal decomposition duration to 6 hours at an L/S (mL/g) ratio of 10 enhances H 2 WO 4 crystallization. Furthermore, experiments without H 2 SO 4 supplementation highlight the system's optimisation potential. Finally, the leaching process was optimised by decreasing H 2 SO 4 concentration to 1 mol/L from 3 mol/L, increasing the temperature to 60°C, and extending the leaching duration to 120 minutes. This leads to a cost-effective synthetic scheelite leaching process with environmental benefits. La production de tungstène se fie principalement à la scheelite, une ressource secondaire en raison de la composition complexe de son minerai et de sa teneur inférieure par rapport à celle de la wolframite à haute teneur. La scheelite synthétique gagne en importance en raison de sa faible teneur en impuretés et son accessibilité dans les investigations en cours en laboratoire. Des progrès récents offrent une méthode de lixiviation réalisable et écologique utilisant une solution mixte de H 2 SO 4 et de H 2 O 2 sous une pression normale et à des températures modérées. Cependant, il manque des recherches approfondies sur cette nouvelle méthode, mettant l'emphase sur le besoin d'une exploration collaborative et d'une optimisation opérationnelle. Le travail courant vise à fournir des connaissances et des améliorations dans l'utilisation des réactifs pour favoriser la durabilité économique et environnementale. Une investigation détaillée du procédé de décomposition thermique a également été entreprise sans compromettre l'efficacité de la lixiviation. Les résultats suggèrent le potentiel d'un recyclage écologique du lixiviat avec une réduction de niveaux de produits chimiques, diminuant les coûts opérationnels. Notamment, l'optimisation de la durée de décomposition thermique à 6 heures à un rapport L/S (ml/g) de 10 améliore la cristallisation de H 2 WO 4 . De plus, des expériences sans supplémentation en H 2 SO 4 soulignent le potentiel d'optimisation du système. Finalement, on a optimisé le procédé de lixiviation en diminuant la concentration de H 2 SO 4 de 3 mol/L à 1 mol/L, en augmentant la température à 60°C et en étendant la durée de lixiviation à 120 minutes. Cela conduit à un procédé de lixiviation de la scheelite synthétique qui est économique avec des avantages environnementaux.

Continuous-running Experiment for Direct Solvent Extraction of Tungsten from Autoclave-soda Leaching Liquor of Scheeite

Thermodynamics of (Ca(OH)2-)NaOH-Na2WO4-H2O and (Ca(OH)2-)NaOH-Na3PO4-H2O systems and their application

Selectively extracting H 2 WO 4 of high purity from the H 2 SO 4 decomposition product of scheelite through hydrogen peroxide coordination followed by purification using ion-exchange and solvent extraction and thermal decomposition

An innovative strategy for deeply separating macro amounts of molybdenum from tungstate solutions via vulcanization step-by-step and microbubble floating-extraction: Theoretical and experimental investigation

Direct Tungsten Extraction from Scheelite in a Molten Salt Media

Extraction and separation of tungsten from acidic high-phosphorus solution

The Application of Zinc Catalyst in the Coal Thermal Solvent Extraction

Complexation extraction of scheelite and transformation behaviour of tungsten-containing phase using H2SO4 solution with H2C2O4 as complexing agent

New Process of Leaching of Molybdenum and Tungsten From Rough Concentrate of Low-grade Molybdenum Oxidation Ore

Selective Solvent Extraction of Vanadium Over Chromium from Alkaline Leaching Solution of Vanadium Slag by D2EHPA/TBP

A Pilot Scale Test Study with Theoretical Justification of Reaction Mechanism for the Recovery of Chromium(vi) Based on Solvent Extraction Using Novel Centrifugal Extractors

Solvent Extraction of Vanadium From Acidic Leaching Solution of Stone Coal

A cleaner and sustainable method to recover vanadium and chromium from the leaching solution based on solvent extraction

Extraction of chromium from tannery sewage sludge

Separation of Vanadium and Tungsten in Roasting‐acid Leaching Solutions of the Spent Selective Catalytic Reducing Denitration Catalyst by Co‐extraction Using Hydroxyoxime Extractant‐quaternary Ammonium Salt Extractant LIX984–N263 Extractant

Sustainable Selective Recovery of Sulfuric Acid and Vanadium from Acidic Wastewater with Two-Step Solvent Extraction

An optimisation study for leaching synthetic scheelite in H2SO4 and H2O2 solution

Recovery of Chromium(vi) in Wastewater Using Solvent Extraction with Amide

Removal and Recovery of Arsenic(III) from Hydrochloric Acid Leach Liquor of Tungsten Slag by Solvent Extraction with 2-Ethylhexanol

Recovery of Vanadium and Chromium from Leaching Solution of Sodium Roasting Vanadium Slag by Stepwise Separation Using Amide and EHEHPA

Deep understanding of sustainable vanadium recovery from chrome vanadium slag: Promotive action of competitive chromium species for vanadium solvent extraction