Improved Na-storage Cycling of Amorphous-Carbon-sheathed Ni3S2 Arrays and Investigation by in Situ TEM Characterization

Xue Xia,Qiannan Wang,Qi Zhu,Jian Xie,Jiangwei Wang,Dagao Zhuang,Shichao Zhang,Gaoshao Cao,Xinbing Zhao

DOI: https://doi.org/10.1016/j.mtener.2017.05.003

IF: 9.257

2017-01-01

Materials Today Energy

Abstract:The past few years have witnessed increasing attention of sodium ion batteries due to the concerns on the shortage of lithium resources. Great challenge, however, remains to develop anode materials with high capacity and long cycle life. In this work, a binder-free array-type electrode, constructed of nickel sulfide (Ni 3 S 2 ) nanoparticles encapsulated in amorphous carbon sheath (ACS), was fabricated by a facile templating method. This array-type Ni 3 S 2 /ACS electrode can yield a high initial reversible capacity of 772 mAh g −1 and a long cycle life with a reversible capacity of 440 mAh g −1 retained after 100 cycles. Both ex situ and in situ characterizations reveal that the excellent electrochemical performance of Ni 3 S 2 /ACS electrode originates from the unique array-type structure, in which high activity of Ni 3 S 2 can be obtained by the thin-layered structure and the sodiation-induced volume expansion of Ni 3 S 2 can be effectively accommodated by the carbon sheath and inner space, resulting in a high mechanical stability of the Ni 3 S 2 /ACS rods during cycling. Our results reveal the electrochemical performance and fundamental reaction mechanism of Ni 3 S 2 /ACS during sodiation-desodiation cycles, shedding lights onto the design of novel sulfide-based anodes for sodium ion batteries.