MoS2/NiS2 Composites for Efficient Hydrogen Evolution Both in Acidic and Alkaline Media

Jue Hu,Chengxu Zhang

DOI: https://doi.org/10.1149/ma2019-01/29/1448

2019-01-01

Abstract:The growing concern about global warming, environmental pollution and energy security has raised the demand for clean energy resources in place of fossil fuel. Cost-efficient generation of hydrogen from water-splitting through electrocatalysis holds tremendous promise for clean energy ( 1, 2 ). Central to the electrocatalysis are efficient and robust electrocatalysts composed of earth-abundant elements, which are urgently needed for realizing low-cost and high-performance energy conversion devices. Transition metal compounds (TMCs) are a group of attractive noble-metal-free electrocatalysts for the hydrogen evolution reaction (HER). Earth-abundant MoS 2 has emerged as a promising hydrogen evolution reaction (HER) catalyst with high activity and durability, but it is kinetically retarded in alkaline media . Extensive efforts have been devoted to improving the HER activity of MoS 2 in acid ( 3 ), but little attention has been paid to simultaneously enhancing its HER performance both in acid and base. This work demonstrates a dramatic enhancement of HER kinetics both in acidic and alkaline media by hybridizing vertical MoS 2 with another earth-abundant material, nickel disulfide (NiS 2 ). Field-emission SEM image shows that the MoS 2 /NiS 2 composite is composed of a film-like structure of NiS 2 cover on the edge surfaces of the MoS 2 sheets (Figure 1a). As shown in Figure 1b, the XRD peaks observed at 2θ=14.1°, 32.9° and 58.8° of the MoS 2 /NiS 2 sample can be indexed to 2H-MoS 2 crystal (JCPDS No. 75-1539), and peaks at 2θ=31.4°, 45.1° and 53.4° indexed to (200), (220) and (311) facets of the NiS 2 , respectively (JCPDS No. 88-1709). The synthesized MoS 2 /NiS 2 composite exhibits a much lower HER overpotential both in acidic and alkaline media than that of bare MoS 2 and NiS 2 catalysts (Figure 1c and d). Figure caption Figure 1. (a) FESEM image of the MoS 2 /NiS 2 composite. (b) XRD patterns of the NiS 2 and MoS 2 /NiS 2 samples, together with the standard pattern of 2H MoS 2 (JCPDS 75-1539) and NiS 2 (JCPDS 88-1709). (c) Polarization curves of bare MoS 2 , NiS 2 and MoS 2 /NiS 2 composite catalysts in 0.5 M H 2 SO 4 solution at a scan rate of 5 mV/s. (d) Polarization curves of bare MoS 2 , NiS 2 and MoS 2 /NiS 2 composite catalysts in 1 M KOH solution at a scan rate of 5 mV/s. References D. Strmcnik et al. , Improving the hydrogen oxidation reaction rate by promotion of hydroxyl adsorption. Nat. Chem. 5 , 300-306 (2013). Y. Jiao, Y. Zheng, M. T. Jaroniec, S. Z. Qiao, Design of electrocatalysts for oxygen- and hydrogen-involving energy conversion reactions. Chem. Soc. Rev. 44 , 2060-2086 (2015). J. Hu et al. , Engineering stepped edge surface structures of MoS 2 sheet stacks to accelerate the hydrogen evolution reaction. Energy Environ. Sci. 10 , 593-603 (2017). Figure 1