Abstract:The spinel LiMn 2 O 4 was synthesized by high temperature solid-state reaction and modified by coating carbon nanotubes (CNTs) which was used as the carbon source. The effect of different coated quantity on the electrochemical performance of spinel cathode materials was discussed. The morphology and structure of the material was characterized by SEM and XRD. The results indicated that the crystal grew well and morphology displayed excellently. Based on electrochemical performance test, the conclusion could be drawn: at 0.5C1C2C rate, the initial discharge capacity of LiMn 2 O 4 coated by 5%wt CNTs was 100.5113.1103.6mAh/g respectively. After 20 cycles, the capacity maintained at 115.5111.3101.1mAh/g, which displayed better capacity retention.

Synthesis and Electrochemical Performance of Spinel LiMn&lt;sub&gt;2&lt;/sub&gt;O&lt;sub&gt;4&lt;/sub&gt; Modified by CNTs

Synthesis and Electrochemical Performance of Spinel LiMn<sub>2</sub>O<sub>4</sub> Modified by CNTs