Experimental Study on Glass-Ceramics Preparation from Hot Steel Slag

Kai Zhang,Chao Deng,Jiakuan Yang

2010-01-01

Abstract:When liquid steel slag produced from steelmaking process was treated into the post-cold slag by conventional methods,the great deal of slag heat was dissipated into the environment,causing a lot of energy waste and environmental pollution.In this study,a novel approach of direct utilization of hot steel slag as a raw material and slag heat for the production of glass-ceramics was proposed and experimentally tested.In order to simulate liquid slag from steelmaking electric furnace,40%water-quenched slag was remelted at 1 450℃and then mixed with 60%melting additives(silica powder,alumina powder and sodium oxide, etc.)and subsequently melted together at 1 500℃for 1 h into modified liquid slag which was cast,heat-treated, annealed and transformed into glass-ceramics.The heat-treated glass samples were investigated using differential thermal analysis(DTA),X-ray diffraction(XRD),and scanning electron microscopy(SEM). The results show that dominant crystalline phase is diopside[CaFe(SiO_3)_2]and the shape of the crystal is like the granule,diameter is about 0.2 -0.6μm.A glass-ceramic with nucleation temperature of 695℃for two hours and crystallization temperature of 893℃for one hour and 1 163℃for half-hour exhibited the best combination of properties.This method of slag mixed with melting additives to adjust the composition of the parent glass is important for the industrial production of glass-ceramics by direct utilization of hot steel slag.