Abstract:Zinc (Zn), magnesium (Mg), and their respective alloys have attracted great attention as biodegradable bone-implant materials due to their excellent biocompatibility and biodegradability. However, the poor mechanical strength of Zn alloys and the rapid degradation rate of Mg alloys limit their clinical application. The manufacture of Zn and Mg bimetals may be a promising way to improve their mechanical and degradation properties. Here we report on Zn/Mg multilayered composites prepared via an accumulative roll bonding (ARB) process. With an increase in the number of ARB cycles, the thicknesses of the Zn layer and the Mg layer were reduced, while a large number of heterogeneous interfaces were introduced into the Zn/Mg multilayered composites. The composite samples after 14 ARB cycles showed the highest yield strength of 411±3 MPa and highest ultimate tensile strength of 501±3 MPa among all the ARB processed samples, significantly higher than those of the Zn/Zn and Mg/Mg multilayered samples. The Zn and Mg layers remained continuous in the Zn/Mg composite samples after annealing at 150 °C for 10 min, resulting in a decrease in yield strength from 411±3 MPa to 349±3 MPa but an increase in elongation from 8±1% to 28±1%. The degradation rate of the Zn/Mg multilayered composite samples in Hanks' solution was ranged from 127±18 µm/y to 6±1 µm/y. The Zn/Mg multilayered composites showed over 100% cell viability with their 25% and 12.5% extracts in relation to MG-63 cells after culturing for 3 d, indicating excellent cytocompatibility. STATEMENT OF SIGNIFICANCE: This work reports a biodegradable Zn/Mg multilayered composite prepared by accumulative roll bonding (ARB) process. The yield and ultimate tensile strength of the Zn/Mg multilayered composites were improved due to grain refinement and the introduction of a large number of heterogeneous interfaces. The composite samples after 14 ARB cycles showed the highest yield strength of 411±3 MPa and highest ultimate tensile strength of 501±3 MPa among all the ARB processed samples. The degradation rate of the Zn/Mg multilayered composite meets the required degradation rate for biodegradable bone-implant materials. The results demonstrated that it is a very promising approach to improve the strength and biocompatibility of biodegradable Zn-based alloys.

Improvement of the Mechanical Properties and Corrosion Resistance of Biodegradable Β-Ca 3 (PO 4 ) 2 /Mg-Zn Composites Prepared by Powder Metallurgy: the Adding Β-Ca 3 (PO 4 ) 2, Hot Extrusion and Aging Treatment

Improvement of the mechanical properties and corrosion resistance of biodegradable β-Ca3(PO4)2/Mg-Zn composites prepared by powder metallurgy: the adding β-Ca3(PO4)2, hot extrusion and aging treatment

In Vitro Corrosion Behavior and in Vivo Biodegradation of Biomedical Β-Ca3(po4)2/mg–zn Composites

Mechanical Properties and Biodegradable Behavior of Mg–6%Zn–Ca3(PO4)2 Metal Matrix Composites in Ringer's Solution

Research on corrosion behavior and biocompatibility of a porous Mg-3%Zn/5%β-Ca3(PO4)2 composite scaffold for bone tissue engineering

Fabrication and Corrosion Properties of Mg-6％Zn-10％(β-Ca3(PO4)2) Composite

Research on corrosion behavior and biocompatibility of a porous Mg–3%Zn/5%β-Ca(PO) composite scaffold for bone tissue engineering

Effects of Zn Concentration and Heat Treatment on the Microstructure, Mechanical Properties and Corrosion Behavior of As-Extruded Mg-Zn Alloys Produced by Powder Metallurgy

Mechanical Properties and Corrosion Resistance of Powder Metallurgical Mg-Zn-Ca/Fe Bulk Metal Glass Composites for Biomedical Application

Microstructure, anticorrosion, biocompatibility and antibacterial activities of extruded Mg−Zn−Mn strengthened with Ca

In Situ Phosphorus-Modified Mg2Ge/Zn-Cu Composite with Improved Mechanical, Degradation, Biotribological Properties, and in Vitro and in Vivo Osteogenesis and Osteointegration Performance for Biodegradable Bone-Implant Applications

Enhanced Corrosion Resistance and Biocompatibility of Biodegradable Magnesium Alloy Modified by Calcium Phosphate/collagen Coating

A biodegradable in situ Zn–Mg2Ge composite for bone-implant applications

Investigating the mechanical properties and corrosion resistance of extruded Mg-1Zn-xCaO (x=0, 0.5, 1.0 wt%) materials

Preparation and characterization of a new biomedical Mg-Zn-Ca alloy

Mechanical properties, corrosion behavior, and cytotoxicity of biodegradable Zn/Mg multilayered composites prepared by accumulative roll bonding process

Preparation and in Vitro Degradation of the Composite Coating with High Adhesion Strength on Biodegradable Mg–Zn–Ca Alloy

Microstructure Evolution and Properties of β-TCP/Mg-Zn-Ca Biocomposite Processed by Hot Extrusion Combined with Multi-Pass ECAP

In Vivo Biocompatibility and Biodegradation of A Mg-15%Ca-3(Po4)(2) Composite As an Implant Material

Corrosion Resistance and Biocompatibility of Calcium Phosphate Coatings with a Micro-Nanofibrous Porous Structure on Biodegradable Magnesium Alloys

In Vivo Degradation and Bone Response of A Composite Coating on Mg-Zn-Ca Alloy Prepared by Microarc Oxidation and Electrochemical Deposition