Abstract:Nonaqueous sol-gel syntheses have been used to make many types of metal oxide nanocrystals. According to the current paradigm, nonaqueous syntheses have slow kinetics, thus favoring the thermodynamic (crystalline) product. Here we investigate the synthesis of hafnium (and zirconium) oxide nanocrystals from the metal chloride in benzyl alcohol. We follow the transition from precursor to nanocrystal through a combination of rheology, EXAFS, NMR, TEM and X-ray total scattering (PDF analysis). Upon dissolving the metal chloride precursor, the exchange of chloride ligands for benzylalkoxide liberates HCl. The latter catalyzes the etherification of benzyl alcohol, eliminating water. During the temperature ramp to the reaction temperature (220 °C), sufficient water is produced to turn the reaction mixture into a macroscopic gel. Rheological analysis shows a network consisting of strong interactions with temperature dependent restructuring. After a few minutes at the reaction temperature, crystalline particles emerge from the gel, and nucleation and growth are complete after 30 minutes. In contrast, four hours are required to obtain the highest isolated yield, which we attribute to the slow in situ formation of water (the extraction solvent). We used our mechanistic insights to optimize the synthesis, achieving high yields with a reduced reaction time. In summation, our results oppose the idea that nonaqueous sol-gel syntheses necessarily form crystalline products slowly, without a transient gel state.

Solution Method for Synthesizing Nanocrystal of Metal Oxide

Mechanochemical Nonhydrolytic Sol–Gel-Strategy for the Production of Mesoporous Multimetallic Oxides

A feasible strategy to balance the crystallinity and specific surface area of metal oxide nanocrystals

Single-Crystalline Dendritic Bimetallic And Multimetallic Nanocubes

Direct Thermal Decomposition of Metal Nitrates in Octadecylamine to Metal Oxide Nanocrystals.

A Novel Molten Salt Mediated Synthesis of Mesoporous Metal Oxides with High Crystallization

Nanomaterials Via Solution Combustion Synthesis: a Step Nearer to Controllability

Sub-2 Nm SnO2 Nanocrystals: A Reduction/oxidation Chemical Reaction Synthesis and Optical Properties

Synthesis Of Nio Nano-Crystal Powders By Molten Salt Method

Effective Octadecylamine System for Nanocrystal Synthesis.

A novel method for synthesizing one or two-dimensional metal oxide (hydroxide) nanomaterials using deep eutectic solvents

From Gel to Crystal: Mechanism of HfO2 and ZrO2 Nanocrystal Synthesis in Benzyl Alcohol

Solution-phase synthesis of transition metal oxide nanocrystals: Morphologies, formulae, and mechanisms

Synthesis of nanocrystalline conducting composite oxides based on a non-ion selective combined complexing process for functional applications

Synthesis of ZnO Nano-crystal Powder by Molten Salt Method

Systematic synthesis of ZnO nanostructures.

Preparation of Nanocrystalline Metal Oxide Powders with the Surfactant-Mediated Method

The synthesis of metal oxide nanowires by directly heating metal samples in appropriate oxygen atmospheres

Design and synthesis of self-ordered mesoporous nanocomposite through controlled in-situ crystallization

A General Strategy for Nanocrystal Synthesis

Continuous Growth Synthesis of Zinc Oxide Nanocrystals with Tunable Size and Doping