Enhancement of Thermal Stability in Bismuth Phosphate by Ln3+ Doping for Tailored Luminescence Properties
Yunlong Zheng,Liping Li,Minglei Zhao,Jing Zheng,Guangshe Li,Errui Yang,Xitian Zhang
DOI: https://doi.org/10.1039/c3ce41960f
IF: 3.756
2014-01-01
CrystEngComm
Abstract:Bismuth phosphate represents one promising class of luminescent host materials, while its application is challenged by structural instability. In this work, a series of nanocrystals Bi(1-x)Ln(x)PO(4) (x = 0.02-0.09; Ln = La, Ce, Nd, Eu, Er) were prepared with an aim to find new routes in improving the structural stability of BiPO4 nanocrystals. Systematic sample characterization by XRD, SEM, TEM, and EDX indicates that doping a small amount of Ln(3+) ions <= 9% could significantly stabilize the low temperature monoclinic phase (LTMP) by retarding the structure transition to the high temperature monoclinic phase (HTMP). For instance, after annealing at 900 degrees C, the relative contents of LTMP for co-doping of 5% La3+, 5% Nd3+, 5% Ce3+ with 2% Eu3+ were as high as 89%, 87%, and 96%, respectively, which are totally different from the un-doped BiPO4 at this temperature where LTMP is absent completely. This phenomenon has never been reported before for improving the stability of BiPO4, which has been explained in terms of lattice disorder due to the preference of the linking ways of rare earth-oxygen polyhedra and PO4 tetrahedra. With this abnormal structural stabilization, the luminescent properties of the Ln(3+) doped LTMP, including emission intensity, lifetime, and quantum efficiency, were further tailored through simply tuning the calcination temperatures.