Abstract:Three-dimensional (3D) extrusion bioprinting has emerged as one of the most promising biofabrication technologies for preparing biomimetic tissue-like constructs. The successful construction of cell-laden constructs majorly relies on the development of proper bioinks with excellent printability and cytocompatibility. Bioinks based on gelatin methacryloyl (GelMA) have been widely explored due to the excellent biocompatibility and biodegradability and the presence of the arginine-glycine-aspartic acid (RGD) sequences for cell adhesion. However, such bioinks usually require low-temperature or ionic cross-linking systems to solidify the extruded hydrogel structures, which results in complex processes and limitations to certain applications. Moreover, many current hydrogel-based bioinks, even after chemical cross-linking, hardly possess the required strength to resist the mechanical loads during the implantation procedure. Herein, we report a self-healing hydrogel bioink based on GelMA and oxidized dextran (OD) for the direct printing of tough and fatigue-resistant cell-laden constructs at room temperature without any template or cross-linking agents. Enabled by dynamic Schiff base chemistry, the mixed GelMA/OD solution showed the characteristics of a dynamic hydrogel with shear-thinning and self-supporting behavior, which allows bridging the 5 mm gap and efficient direct bioprinting of complex constructs with high shape fidelity. After photo-cross-linking, the resulting tissue constructs exhibited excellent low cell damage, high cell viability, and enhanced mechanical strength. Moreover, the GelMA/OD construct could resist up to 95% compressive deformation without any breakage and was able to maintain 80% of the original Young's modulus during long-term loading (50 cycles). It is believed that our GelMA/OD bioink would expand the potential of GelMA-based bioinks in applications such as tissue engineering and pharmaceutical screening.

3D Bioprinting of Self‐Standing Silk‐Based Bioink

3D freeform printing of silk fibroin

Inkjet Bioprinting of 3D Silk Fibroin Cellular Constructs Using Sacrificial Alginate

Precisely Printable Silk Fibroin/Carboxymethyl Cellulose/Alginate Bioink for 3D Printing

3D Bioprinting of Low-Concentration Cell-Laden Gelatin Methacrylate (gelma) Bioinks with a Two-Step Cross-linking Strategy.

Sacrificial Microgel-Laden Bioink-Enabled 3D Bioprinting of Mesoscale Pore Networks

3D Bioprinting of shear-thinning hybrid bioinks with excellent bioactivity derived from gellan/alginate and thixotropic magnesium phosphate-based gels

Instant Gelation System As Self-Healable and Printable 3D Cell Culture Bioink Based on Dynamic Covalent Chemistry.

3D bioprinted silk fibroin hydrogels for tissue engineering

3D Printing Silk-Gelatin-propanediol Scaffold with Enhanced Osteogenesis Properties Through P-Smad1/5/8 Activated Runx2 Pathway

3D-Printable Supramolecular Hydrogels with Shear-Thinning Property: Fabricating Strength Tunable Bioink Via Dual Crosslinking.

A biocompatible pea protein isolate-derived bioink for 3D bioprinting and tissue engineering

A Silk Fibroin Methacryloyl-Modified Hydrogel Promoting Cell Adhesion for Customized 3D Cell-Laden Structures

3D Printing of Silk Particle-Reinforced Chitosan Hydrogel Structures and Their Properties.

Aqueous Two‐Phase Emulsion Bioink‐Enabled 3D Bioprinting of Porous Hydrogels

Direct 3D Printed Biomimetic Scaffolds Based on Hydrogel Microparticles for Cell Spheroid Growth

Double-Network Hydrogel 3D BioPrinting Biocompatible with Fibroblast Cells for Tissue Engineering Applications

Evaluation of silk-based bioink during pre and post 3D bioprinting: A review

3D Printing of Cell‐Laden Microgel‐Based Biphasic Bioink with Heterogeneous Microenvironment for Biomedical Applications

Direct 3D Bioprinting of Tough and Antifatigue Cell-Laden Constructs Enabled by a Self-Healing Hydrogel Bioink.

3D Bioprinting of Gellan Gum and Poly (ethylene Glycol) Diacrylate Based Hydrogels to Produce Human-Scale Constructs with High-Fidelity