Abstract:Fluoropolymer microtubes with a smooth surface were fabricated in more than 70% yield via reversible addition fragmentation chain transfer (RAFT) co-polymerization of N,N-methylene bisacrylamide (MBA) gel fibers as both template and monomer, 2-(perfluoro-3-methylbutyl)ethyl acrylate (R-3420) as co-monomer, and pentaerythritol tetraacrylate (PET4A) as cross-linker. The resulting fluoropolymer microtubes were characterized fully by SEM, TEM, EDS, XPS, and FT-IR. The influence of the monomer composition on the yields and morphologies of the tubes were investigated in detail. The results indicated that polymer microtubes with a smooth surface were obtained at suitable amounts of R-3420 and PET4A. Because of the decreased solubility of MBA gel fibers, the wall thickness increased as more R-3420 was used. In the presence of PET4A, the solution polymerization could be facilitated and more R-3420 could be attached onto the tubes based on FT-IR analysis. The water contact angle and swelling ratio measurements both revealed the low hydrophilicity and high lipophilicity of the fluoropolymer microtubes, which made the sample able to absorb toluene selectively in a water/toluene two-phase system.

Fabrication of Rectangular 2,6-Diamino-3,5-dinitropyrazine-1-oxide Microtubes

Preparation and characterization of rectangular tin dioxide microtubes

Fabrication at room temperature of uniform mesopore partially carbonized microtubes via an interface reaction

Zinc Oxide Microtubes Prepared by Optical Thermal Evaporation

Single Crystalline Submicrotubes from Small Organic Molecules

Fabrication of Fluoropolymer Microtubes Via RAFT Copolymerization of N,N'-Methylene Bisacrylamide Gel Fibers and Fluoromonomer.

Controllable Synthesis of the Six Prism Zinc Oxide Microtubes and 3D Microflowers Consist of the Six Prism Microrobs

Lead Titanate Nano- and Microtubes

Lithium Niobate Microtubes Within Ordered Macroporous Silicon by Templated Thermolysis of A Single Source Precursor

Preparation of polymer microtubes via RAFT polymerization of N, N'-methylene bisacrylamide gel fibers

Fabrication of Tubular ZnO by Vesicle–template Fusion

Polygonal Single‐Crystal Aluminum Borate Microtubes

Fabrication of ZnO Microtubes with Adjustable Nanopores on the Walls by the Templating of Butterfly Wing Scales

Hydrothermal Synthesis of Prismatic NaHoF4 Microtubes and NaSmF4 Nanotubes.

Fabrication of ZnO Microtubes by Using Electrospun Polymer Fiber Templates

Facile Fabrication of Free-Standing Microtubes Composed of Colloidal Spheres

Remarkable Hexagonal Carbon Tubes Transformed from Zinc Tetrapyridylporphine

Fabrication of Carboxyl-Functionalized Polymer Microtubes Via RAFT Copolymerization of Diurea-Type Xerogel Fibers and Acrylic Acid

In Situ Etching Strategy to Controllably Fabricate Single-Crystal Metal–Organic Framework Microtubes

Rectangular Single-Crystal Mullite Microtubes

Controllable Preparation of Microscale Tubes with Multiphase Co-Laminar Flow in a Double Co-Axial Microdevice