Abstract:A network polymer at its gel point is in a critical state between liquid and solid. Linear viscoelasticity reduces to a simple behavior which is described by the gel equation for the stress (J. Rheol., 30, 367 (1986) and 31, 683 (1987)):$$ \tau (\rm{t}) = \int_{ - \infty }^{\rm{t}} {{\rm{S}}\quad {{({\rm{t}} - {\rm{t'}})}^{ - {\rm{n}}}}} \dot{\gamma} ({\rm{t'}}){\rm{dt}}$$in which the strain history is defined by the rate of deformation tensor$$ \dot{\gamma} ({\rm{t'}})$$. Molecular parameters determine the gel strength, S, and the relaxation exponent, n. The above power law relaxation behavior seems to be a universal property at the gel point. It has been found with a large variety of chemically or physically crosslinking polymers, i.e. with all crosslinking polymers which we studied above the glass transition temperature. Initially, we seemed to find a universal relaxation exponent of 0.5 for all gels as it might be expected for a critical state. However, measured values between 0.15 and 0.8 indicate that the relaxation exponent may cover the entire range between 0 and 1. The front factor S depends on the magnitude of the relaxation exponent, and for classes of network polymers it is found to follow the relation S=Goλon, where Go and λo are characteristic properties which are constant within each class of network polymers (to appear in Macromolecules, 1990). Go is of the order of the plateau modulus of the network and λo is believed to be the relaxation time of a network strand. The universality of the power law relaxation behavior of polymers at the gel point allows a most accurate determination of the instant of gelation (Polym. Eng. Sci., 27,1698 (1987)). The gel point is reached when the complex rheological behavior reduces to power law relaxation in the terminal frequency range (fractal behavior, mechanical selfsimilarity). The simple technique of Fourier Transform Mechanical Spectroscopy (J. Non-Newt. Fluid Mech., 27, 17 (1988)) not only allows the direct determination of the gel point. It also allows, by extrapolation, to predict the distance from the gel point in a sol. Recent advances of the technique and a set of applications will be given. When replacing the rate of deformation tensor in the gel equation with a suitable strain measure, it can predict the stress in critical gels up to about 2 strain units (for PDMS). Beyond this, a large strain will irreversibly rupture the molecular network.

Non-Debye Stress Relaxation in Green Silica Gel

Glass Transition in Gels

Physically-based Interpretation of Abnormal Stress Relaxation Response in Glassy Polymers

Quantitative analysis of the structural relaxation of silica-PEO shake gel by X-ray and light scattering

Stretched Exponential Relaxation of Glasses: Origin of the Mixed Alkali Effect

Stress Relaxation of Near-Critical Gels

New Kinetics Equation for Stress Relaxation of Semi-crystalline Polymers below Glass Transition Temperature

Experimental studies on the relaxation behavior of commercial polymer melts

Stress amplification and relaxation imaging around cracks in nanocomposite gels using ultrasound elastography

Analysis of linear viscoelastic behaviour of alginate gels: effects of inner relaxation, water diffusion, and syneresis

Rheology of Polymer Gels

Interplay between shear loading and structural aging in a physical gel

Wrinkling of a Polymeric Gel During Transient Swelling

Long-time structural relaxation of glass-forming liquids: Simple or stretched exponential?

Nonergodic Dynamics of A Novel Thermally Sensitive Hybrid Gel

Residual stresses and shear-induced overaging in boehmite gels

Structural Relaxation of a Gel Modeled by Three Body Interactions

Physical aging and relaxation of residual stresses in a colloidal glass following flow cessation

Structural, shear and volume relaxation in a commercial float glass during aging

Nonlinear stress relaxation and failure of time‒strain separability of aqueous poly(ethylene oxide)/silica nanoparticle mixtures

Relaxation processes of densified silica glass