Abstract:The nanostructure‐controllable TaSi2 arrays with vertically aligned nanotips are produced through a novel and straightforward method, involving advanced directional solidification, heat treatment, and etching process. The enhanced sharpness and high regularity of the TaSi2 nanotip array contribute to its favorable field emission performance, thereby advancing the potential application of TaSi2 as a cold cathode material in electronic devices. Recognizing the strong potential of cold cathodes for important commercial applications in fields such as electronics, there is a growing interest in the exploration of novel 1D nanomaterials. Among various cold cathode materials, TaSi2 is of great interest for its outstanding field emission performance. In this work, the Si‐TaSi2 eutectic composite with nano‐sized highly oriented TaSi2 fibers and semi‐coherent phase interfaces is prepared by the laser floating zone melting technique with a very high‐temperature gradient of 6000 K cm−1 at a solidification rate of 200 μm s−1. On the basis of directionally solidified Si‐TaSi2 eutectic composite, well‐aligned TaSi2 nanorod and nanotip arrays are fabricated by inductively coupling plasma (ICP) etching process and HNO3/HF wet etching process, respectively. The field emission measurements show that the field enhancement factor, turn‐on electric field, and effective work function are strongly affected by tip morphologies. The TaSi2 array with regular nanotip structure possesses the best field emission characteristic among all TaSi2 nanostructures, with a relatively low turn‐on field of 4.8 V μm−1 and a high current density of 733 μA cm−2. These findings preliminarily establish a clear relationship between the performance and structure of the array, providing technical guidance for the application of this material in electronic devices.

Preparation and Field-Emission of TaSe2 Nanobelt Quasi-Arrays, and Electrical Transport of Its Individual Nanobelt

Preparation and field-emission of tase 2nanobelt quasi-arrays, and electrical transport of its individual nanobelt

Fabrication of TaS2 Nanobelt Arrays and Their Enhanced Field-Emission

Synthesis and Characterization of Bi2S3 Quantum Dot-Sensitized TiO2 Nanorod Arrays Coated with ZnSe Passivation Layers

Tantalum Disulfide Nanobelts: Preparation, Superconductivity And Field Emission

Centimeter-Long Ta3n5 Nanobelts: Synthesis, Electrical Transport, and Photoconductive Properties

Hot electron field emission via individually transistor-ballasted carbon nanotube arrays.

Insight into TaSi2 Nanostructures with Different Morphologies and Their Field Emission Properties

Using Nanoscale Thermocapillary Flows to Create Arrays of Purely Semiconducting Single-Walled Carbon Nanotubes

Fabrication and field-emission performance of zirconium disulfide nanobelt arrays.

NbN and NbS2 nanobelt arrays: in-situ conversion preparation and field-emission performance.

Metallic vs. Semiconducting Properties of Quasi-One-Dimensional Tantalum Selenide van der Waals Nanoribbons

Synthesis and Field Emission Properties of Topological Insulator Bi2Se3nanoflake Arrays

Enhanced field emission and patterned emitter device fabrication of metal-tetracyanoquinodimethane nanowires array

Controlled growth and field-emission properties of NbSe 2 micro/nanostructured films

Observation of Charge Density Wave Transition in TaSe3 Mesowires

Crystal Orientation-Ordered ZnS Nanobelt Quasi-Arrays and Their Enhanced Field-Emission.

Controlled Growth and Field-Emission Properties of NbSe2 Micro/nanostructured Films.

Synthesis and nano-field-effect transistors of p-type Zn0.3Cd0.7Te nanoribbons

Observation of Topological Electronic Structure in Quasi-1D Superconductor TaSe3

Preparation and Field Emission Properties of Titanium Polysulfide Nanobelt Films