Water-Soluble Poly(phenylene ethynylene)s that Contain Phosphonium Pendant Groups

Kirk Schanze,Isaí Barboza-Ramos,Habtom Gobeze,Daniel Wherrit

DOI: https://doi.org/10.26434/chemrxiv-2024-4x2d0

2024-01-22

Abstract:Expanding the functionality of conjugated polyelectrolytes (CPEs) is important for polymer- mediated biosensing applications. The current study reports the design and synthesis of a novel class of water-soluble poly(phenylene ethynylene) (PPE)-based CPEs, featuring cationic trimethyl phosphonium (-PMe3+) moieties as pendant groups. A series of four CPEs were prepared which vary in the number of -PMe3+ groups and the length of the side-chains linking the phosphonium groups to the PPE backbone (3- or 6-carbon linkers). The polymers’ molecular weights (MW) were estimated by diffusion-ordered NMR spectroscopy (DOSY) in methanol relative to poly(ethylene glycol) standards, and MW values ranging from 10 – 30 kD were recovered. The photophysical properties of the new CPEs were assessed by steady state and time-resolved fluorescence spectroscopy analysis, using polymer solutions in water and methanol. Interesting relationships were observed between the optical properties and the structural variations of the new CPEs. Namely, the fluorescence reveals that the CPEs aggregate in water, with the degree of aggregation increasing with fewer -PMe3+ groups, and longer side-chains. The fluorescence quantum yields of the CPEs in methanol are high, with one exhibiting > 90% yield. Transient absorption spectroscopy on timescales from picoseconds to microseconds probes the excited state structure and dynamics of the CPEs in water and methanol. The singlet exciton state decays more rapidly in water due to non-radiative decay promoted by aggregation states. Excitation of the polymers produces triplet excitons and studies using singlet oxygen (1O2) phosphorescence and an anthracene-based probe confirm that 1O2 is produced by sensitization. Addition of pyrophosphate (PPi) to the phosphonium CPEs in methanol leads to fluorescence quenching; the mechanism of quenching is attributed to aggregation induced quenching.

Chemistry

What problem does this paper attempt to address?

The paper focuses on the design and synthesis of novel water-soluble conjugated poly(phenylethynylene) (PPE) based copolyelectrolytes (CPEs) containing trimethylphosphine (-PMe3+) cation as the side group. Four different CPEs were prepared with variations in the number of -PMe3+ groups and the side chain length connecting the phosphonic acid group to the PPE backbone. The polymer molecular weight was estimated by diffusion-ordered nuclear magnetic resonance spectroscopy (DOSY), and the photophysical properties of the new CPEs were evaluated by steady-state and time-resolved fluorescence spectroscopy.

In water, these CPEs aggregate, and the degree of aggregation is related to the number of -PMe3+ groups and the longer side chains. In methanol, the CPEs exhibit higher fluorescence quantum yields, with one of the CPEs having a quantum yield exceeding 90%. Transient absorption spectroscopy studied the excited state structure and dynamics of the CPEs on a time scale from picoseconds to microseconds, indicating faster decay of the singlet excited state due to non-radiative processes caused by aggregation in water. Furthermore, the production of singlet oxygen (1O2) by the polymer upon excitation was confirmed by phosphorescence emission of 1O2 and anthracene-based probe.

Fluorescence quenching was observed when pyrophosphate (PPi) was added to methanol solutions of CPEs containing phosphine groups, suggesting quenching induced by aggregation caused by PPi. This study demonstrates the potential of phosphine-containing CPEs as materials for sensing and phototherapy applications and provides a platform for further research.