Hot compression deformation behavior and processing maps of ATI 718Plus superalloy
Jianbo Zhang,Chongji Wu,Yuanyi Peng,Xingchuan Xia,Jingan Li,Jian Ding,Chang Liu,Xueguang Chen,Ji Dong,Yongchang Liu
DOI: https://doi.org/10.1016/j.jallcom.2020.155195
IF: 6.2
2020-09-01
Journal of Alloys and Compounds
Abstract:<p>In this work, hot compression deformation behavior and processing maps of ATI 718Plus superalloy were studied by isothermal compression test on Gleeble-3800 thermal simulation testing machine. The results showed that under the present conditions (with deformation temperature range of 1030–1180 °C, strain rate of 0.01–10 s<sup>−1</sup> and deformation amount of 50%), flow stress decreased with the increasing of deformation temperature and decreasing of strain rates. Meanwhile, simplified and strain-compensated classical Arrhenius constitutive equation models were established respectively, and strain-compensated constitutive equation improves the accuracy of flow stress prediction. In addition, processing maps showed that the optimal hot processing parameter ranges were 1140–1180 °C with strain rate of 0.01–0.1 s<sup>−1</sup> respectively. The effects of strain rate and deformation temperature on microstructure evolution was investigated and low strain rate and high deformation temperature are conductive to DRX.</p>
materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering