Abstract:ABSTRACT In this work, polylactic acid/polycaprolactone/silk fibroin (PLA/PCL/SF) nanofiber scaffolds with different mass ratios were prepared by electrospinning technology. The morphology and structure of the nanofiber scaffold were characterized with the scanning electron microscope (SEM), and its porosity and adsorption were tested using the Fourier transform infrared spectrometer (FTIR). 24 New Zealand white rabbits were rolled into control group ( n = 8, with autologous tendons) and experimental group ( n = 16) randomly. The PLA/PCL/SF nanofiber scaffolds were adopted to wrap autologous tendons to establish extra-articular models. Tendon-bone healing was evaluated six weeks after surgery through histological and biomechanical tests, and the related gene expressions in tissue cells were detected. It turned out that mass ratio of PLA/PCL and SF components had a considerable impact on the morphology of the nanofiber scaffold. The surface of nanofiber with a mass ratio of 3:1 was distributed with dense pores. As the content of SF increased, the porosity and adsorption of the nanofiber scaffold gradually decreased. Moreover, the experimental results suggested that the addition of SF improved the hydrophilicity of PLA/PCL/SF scaffold, which was beneficial to the adhesion and proliferation of NIH/3T3 (a mouse embryonic fibroblast cell line established by the National Institutes of Health (NIH)). In addition, histological observation results showed that the width of the tendon-bone interface (TBI) of rabbits in control group was still relatively large at the 6th week after the surgery, with poor healing effect and disordered collagen arrangement. The widths of the TBI of the material group and rehabilitation group were substantially narrower relative to that in control group, and the collagen was arranged regularly. It was suggested that the healing effects between tendon and bone in material group and rehabilitation group were accelerated, and the effect in the rehabilitation group was superior to that of material group, indicating that rehabilitation exercise could organize the negative effects of training in postoperative rehabilitation training and promote the healing between tendons and bones.

Induction of Macrophage Polarization by Electrospun Nano-Yarn Containing Naproxen Sodium to Promote Tendon Repair

Integration of mesenchymal stem cell sheet and bFGF-loaded fibrin gel in knitted PLGA scaffolds favorable for tendon repair

Coaxial Electrospun Nanofibrous Membranes as Dual‐Functional Biomimetic Tendon Sheath for Tendon Repair and Anti‐Peritendinous Adhesion

Piezoelectrically-enhanced Composite Membranes Mimicking the Tendinous Electrical Microenvironment for Advanced Tendon Repair

Preparation of Silk Fibroin Nanofiber Scaffold and Its Application in Tendon-Bone Healing and Sports Rehabilitation

Optimization of Intrinsic and Extrinsic Tendon Healing Through Controllable Water-Soluble Mitomycin-C Release from Electrospun Fibers by Mediating Adhesion-Related Gene Expression.

Carbon Fiber-Mediated Electrospinning Scaffolds Can Conduct Electricity for Repairing Defective Tendon

Biomimetic multilayer polycaprolactone/sodium alginate hydrogel scaffolds loaded with melatonin facilitate tendon regeneration

Synergistic Effect of Regeneration and Inflammation Via Ibuprofen-Loaded Electrospun Fibrous Scaffolds for Repairing Skeletal Muscle

Biodegradable Polymer Electrospinning for Tendon Repairment

Bioactive Nanostructured Scaffold-Based Approach for Tendon and Ligament Tissue Engineering

Design of an electrospun tubular construct combining a mechanical and biological approach to improve tendon repair

Parishin A-loaded mesoporous silica nanoparticles modulate macrophage polarization to attenuate tendinopathy

Micropattern Silk Fibroin Film Facilitates Tendon Repair In Vivo and Promotes Tenogenic Differentiation of Tendon Stem/Progenitor Cells through the α2β1/FAK/PI3K/AKT Signaling Pathway In Vitro

Hybrid Nanofibrous Composites with Anisotropic Mechanics and Architecture for Tendon/Ligament Repair and Regeneration

Bi-lineage inducible and immunoregulatory electrospun fibers scaffolds for synchronous regeneration of tendon-to-bone interface

A Janus nanofibrous scaffold integrated with exercise-driven electrical stimulation and nanotopological effect enabling the promotion of tendon-to-bone healing

Design and development of a reinforced tubular electrospun construct for the repair of ruptures of deep flexor tendons

Towards an Ideal Polymer Scaffold for Tendon/Ligament Tissue Engineering

Electrospun PLGA Fiber Diameter and Alignment of Tendon Biomimetic Fleece Potentiate Tenogenic Differentiation and Immunomodulatory Function of Amniotic Epithelial Stem Cells

Pro-chondrogenic and immunomodulatory melatonin-loaded electrospun membranes for tendon-to-bone healing.