A Simple Regeneration Process Using a CO2-switchable Solvent for Cellulose Hydrogels

Masahiro Yoshizawa-Fujita,Arata Matsui,Deandra Ayu Putri,Morgan L. Thomas,Yuko Takeoka,Masahiro Rikukawa
DOI: https://doi.org/10.26434/chemrxiv-2024-b32m2
2024-01-17
Abstract:Cellulose is one of the main components of plant cell walls, abundant on earth, and is a non-edible material that can be acquired at a low cost. Furthermore, there has been increasing interest in its use in environmentally friendly, carbon-neutral, sustainable materials. It is expected that the applications of cellulose will expand with the development of a simple processing method. Previously, it was demonstrated that cellulose can be dissolved in a non-heated, short-duration process using an aqueous pyrrolidinium hydroxide solution. In this study, we dissolved cellulose in aqueous N-butyl-N-methylpyrrolidinium hydroxide solution ([C4mpyr][OH]/H2O) and investigated the cellulose regeneration process based on changes in solubility upon application of CO2 gas. We investigated the effect of transformation of the anion chemical structure on cellulose solubility by flowing CO2 gas into [C4mpyr][OH]/H2O and conducted pH, FT-IR, and 13C NMR measurements. We observed that the changes in anion structure allowed for the modulation of cellulose solubility in [C4mpyr][OH]/H2O, thus establishing a simple and safe cellulose regeneration process. This regeneration process was also applied to enable the production of cellulose hydrogels. The hydrogel formed using this approach was revealed to be of a higher mechanical strength than that of an analogous hydrogel produced using the same dissolution solvent with addition of a cross-linker. The ability to produce cellulose-based hydrogels of different mechanical properties is expected to expand the possible applications.
Chemistry
What problem does this paper attempt to address?
The main problem that this paper attempts to solve is to develop a simple and environmentally - friendly regeneration process for the production of cellulose hydrogels. Specifically, the research aims to dissolve and regenerate cellulose by using carbon dioxide (CO₂) - switchable solvents, thereby avoiding the toxic or harmful chemicals used in traditional methods and improving the mechanical properties and environmental - friendliness of cellulose materials. ### Summary of Main Problems: 1. **Simplify Cellulose Treatment Methods**: Traditional cellulose dissolution and regeneration processes usually require high temperature, high pressure or toxic solvents, which not only consume a lot of energy but may also produce harmful by - products. Therefore, researchers hope to find a milder and safer method to process cellulose. 2. **Improve the Mechanical Properties of Cellulose Hydrogels**: Cellulose hydrogels are widely used in fields such as medicine and sensing, but their mechanical properties (such as strength and elasticity) are crucial for practical applications. This research hopes to produce cellulose hydrogels with higher mechanical strength by improving the regeneration process. 3. **Use CO₂ for Green Chemical Reactions**: CO₂ is one of the main components of greenhouse gases. How to effectively use CO₂ is not only the key to dealing with climate change but also an important way to achieve carbon neutrality. This research proposes a method to regulate the solubility of cellulose by introducing CO₂ gas, thereby realizing the regeneration of cellulose and reducing the impact on the environment at the same time. ### Solutions: - **Solvent Selection**: The researchers selected an aqueous solution of N - butyl - N - methylpyrrolidinium hydroxide ([C₄mpyr][OH]/H₂O) as the solvent for cellulose. This solvent can quickly dissolve cellulose at room temperature without the need for heating or other harsh conditions. - **CO₂ Regulation**: By introducing CO₂ gas into the [C₄mpyr][OH]/H₂O solution, the researchers found that the hydroxide ions (OH⁻) in the solution gradually convert into carbonate ions (CO₃²⁻) and bicarbonate ions (HCO₃⁻), resulting in a decrease in the solubility of cellulose and finally precipitating out to form a hydrogel. - **Mechanical Property Evaluation**: Through compression tests, the researchers found that the cellulose hydrogel regenerated by CO₂ induction exhibits higher mechanical strength (the maximum compressive strength is 1.2 MPa and the fracture strain is 104%), which is superior to hydrogels prepared by other traditional methods. ### Conclusion: This research has successfully developed a simple and environmentally - friendly cellulose regeneration method, and has achieved the efficient preparation of cellulose hydrogels by using CO₂ gas. This method not only avoids the toxic chemicals in traditional methods, but also significantly improves the mechanical properties of cellulose hydrogels, providing new possibilities for the wide application of cellulose materials.