Underwater Drag Reduction and Buoyancy Enhancement on Biomimetic Antiabrasive Superhydrophobic Coatings
Zhaochang Wang,Xiaojun Liu,Jiawei Ji,Tongtong Tao,Tao Zhang,Jimin Xu,Yunlong Jiao,Kun Liu
DOI: https://doi.org/10.1021/acsami.1c14342
2021-09-30
Abstract:A superhydrophobic (SHB) surface with an excellent self-cleaning ability is of great significance in both human survival and industrial fields. However, it is still a challenge to achieve large-area preparation of antiabrasive SHB surfaces with great mechanical robustness for broader applications. Thus, a kind of facile SHB coating with excellent liquid repellency and antiresistance is constructed by spraying a fluorine-free suspension consisting of epoxy resin, hexadecyltrimethoxysilane (HDTMS), and silica nanoparticles on a glass sheet. The SHB coating not only shows high adhesion on various materials but also has high water repellency under various test conditions, including tape peeling after blade scraping, sandpaper abrasion, and immersing in a complex environment. Additionally, the SHB spheres coated with laser-induced microstructure armor could form a continuous gas cavity during the water entry process, which is essential to prolonging the drag reduction ability of SHB coatings in liquid. Finally, the prepared robust SHB coatings have been employed in underwater buoyancy enhancement and reducing fluid resistance, which may open new avenues for underwater drag reduction in the field of marine applications.The Supporting Information is available free of charge at https://pubs.acs.org/doi/10.1021/acsami.1c14342.Photographs of superhydrophobic coatings on different substrates; analysis of surface morphology and chemical composition of superhydrophobic coatings; high-speed camera to capture the bounce of water droplets released from different heights on the coating; images of the immersed superhydrophobic coating; schematic diagram of wetting state transition mechanism; schematic diagram of mechanical stability of composite coating; comparison of the robustness of superhydrophobic coatings; durability of the as-prepared samples in complex environment; the construction of microstructured armor SHB spheres; stability of the cavity on the superhydrophobic sphere under different conditions; two-dimensional profile equation of the liquid–gas intersection at the solid–liquid–gas interface (PDF)Movie S1, rolling angle of a 10 μL water drop (MP4)Movie S2, liquid super-repellency on the superhydrophobic coating (MP4)Movie S3, self-cleaning effect of the superhydrophobic coating (MP4)Movie S4, bouncing of water droplets released from 10 nm on a superhydrophobic coating (MP4)Movie S5, bouncing of water droplets released from 48 nm on a superhydrophobic coating (MP4)Movie S6, wear resistance test on the superhydrophobic coating (MP4)Movie S7, blade scraping test (MP4)Movie S8, water entry process of original sphere with a diameter of 10 mm at a releasing height of 27 mm (MP4)Movie S9, water entry process of superhydrophobic spheres with a smooth surface with a diameter of 10 mm at a releasing height of 27 mm MP4)Movie S10, water entry process of superhydrophobic spheres with Glaco with a diameter of 10 mm at a releasing height of 27 mm (MP4)Movie S11, water entry process of superhydrophobic spheres with microstructures with a diameter of 10 mm at a releasing height of 27 mm (MP4)Movies S12, stability of the gas cavity on the Glaco-coated sphere after 20 times of water entry (MP4)Movie S13, stability of the gas cavity on the superhydrophobic spheres without microstructures after 50 times of water entry (MP4)Movie S14, stability of the gas cavity on the superhydrophobic spheres without microstructures after 80 times of water entry (MP4)Movie S15, stability of the gas cavity on the Glaco-coated sphere after hitting the iron substrate 20 times (MP4)Movie S16, stability of the gas cavity on the superhydrophobic spheres without microstructures after hitting the iron substrate 60 times (MP4)Movie S17, stability of the gas cavity on the superhydrophobic spheres with microstructures after hitting the iron substrate 60 times (MP4)Movie S18, underwater stability test (MP4)(MP4)Movie S19, stability of the gas cavity on the Glaco-coated sphere at 600 rpm (MP4)Movie S20, stability of the gas cavity on the superhydrophobic spheres without microstructures at 1000 rpm (MP4)Movie S21, stability of the gas cavity on the superhydrophobic spheres with microstructures at 1000 rpmMovie S22, buoyancy increase test on the original glass sheet (MP4)Movie S23, buoyancy increase test on the superhydrophobic glass sheet (MP4)Movie S24, sailing test of superhydrophobic model ship (MP4)This article has not yet been cited by other publications.
materials science, multidisciplinary,nanoscience & nanotechnology