Abstract:Self-healing coatings doped by nano-containers loaded with inhibitors have shown remarkable anti-corrosion efficiency and durability in extending metal life and slowing down coating failure. However, low loading capacity of corrosion inhibitors in nano-containers is a problem plaguing the further development and application of smart coatings. In this study, mesoporous silica with large pore sizes (MSN) was synthesized using the soft template method which significantly increased the loading capacity of the corrosion inhibitor, and a smart self-healing composite coating was designed, which could protect carbon steel from corrosion and provide durable protection for it. Specifically, the composite coating (EP/DMTD@MSN-PAA) was prepared by incorporating mesoporous silica nano-containers embedded with 2,5-dimercapto-1,3,4-thiadiazole (DMTD) molecules into the epoxy resin coating. The results of BET test showed that the prepared MSNs had high specific surface area (734.97 m2/g) and large pore volume (0.85 cm3/g). The thermogravimetric (TG) analysis showed 35.7% of loading amount of corrosion inhibitors in the nano-materials. Response release experiments showed that the DMTD@MSN-PAA had of acid-response release characteristics. When pH value of the system decreased from 7 to 3, the release amount of the DMTD molecules increased from 40.3% to 93.7%. The contact angle test showed that the epoxy resin (EP) coating had a contact angle value of 57.7°, while those of the composite coatings doped with 1 wt%, 3 wt% and 6 wt% DMTD@MSN-PAA (EP/DMTD@MSN-PAA) were 65.1°, 75.2° and 67.2°, respectively. These results indicated that the composite coatings had better hydrophobicity compared to the EP coating, and were conducive to prolonging the coating service time. The anti-corrosion performances of both the EP and the composite coatings with different doping amounts of DMTD@MSN-PAA were evaluated by EIS measurements. The R ct value of the EP coating decreased from 190.3 to 25.1 Ω · cm2 within the time of 48 h of immersion in 3.5 wt% NaCl solution, while ones of the EP/DMTD@MSN-PAA coatings doped with 1 wt%, 3 wt% and 6 wt% of DMTD@MSN-PAA increased from 303.1, 720.7.7, 523.4–1426.4, 2113.8, 1066.3 Ω · cm2, respectively. In addition, the corrosion resistance of the EP and composite coatings were further evaluated by etching experiments. The results showed that after 35 d of immersion, compared with that of the EP coating, surface corrosion degree of the composite coatings was lower, and the scaling off speed of the coatings slowed down, which further proved that the composite coating had strong corrosion resistance and special self-healing characteristics.

Design of a smart protective coating with molybdate-loaded halloysite nanotubes towards corrosion protection in reinforced concrete

The new insights towards smart pH-responsive anticorrosion coating based on HNTs carrying synergistic inhibitors: Experimental and molecular simulation

A Novel Dual-Functional Pretreatment Layer for Carbon Steel in Chloride-Contaminated Concrete Pore Solutions

Designing a smart epoxy anti-corrosion coating loaded with molybdate-doped polythiophene nano-hybrid self-assembled multi-walled carbon nanotube

Inhibitor loaded functional HNTs modified coatings towards corrosion protection in reinforced concrete environment

An Intelligent Coating Based on Ph-Sensitive Hybrid Hydrogel for Corrosion Protection of Mild Steel

Construction of smart halloysite nanocontainers for active long-term anticorrosion of epoxy coatings

A New Strategy for Long-Term Smart Corrosion Protection of Q235 Carbon Steel Using Polyaniline Nanofiber Covalently Linking with Modified GO as Reinforcement of Epoxy Coating

Preparation of TEOS-GPTMS-PDMS Hybrid Material and Its Application in the Protection of Concrete

Design, Preparation, and Performance of a Novel Organic–inorganic Composite Coating with High Adhesion and Protection for Concrete

Synergistic inhibition of molybdate and phytate on chloride-induced corrosion of carbon steel in simulated concrete pore solutions

Construction of Smart Coatings Containing Core-Shell Nanofibers with Self-Healing and Active Corrosion Protection

Developing wide pH-responsive, self-healing, and anti-corrosion epoxy composite coatings based on encapsulating oleic acid/ 2-mercaptobenzimidazole corrosion inhibitors in chitosan/poly(vinyl alcohol) core-shell nanofibers

Corrosion protection of 304 stainless steel from a smart conducting polypyrrole coating doped with pH-sensitive molybdate-loaded TiO2 nanocontainers

Enhanced Corrosion Resistance of Reinforcing Steels in Simulated Concrete Pore Solution with Low Molybdate to Chloride Ratios

Multifunctional Inhibition Based on Layered Double Hydroxides to Comprehensively Control Corrosion of Carbon Steel in Concrete

Smart nanoarchitectonics of epoxy coating: Preparation, release behavior and self-healing performance based on mesoporous silica nano-containers loaded with DMTD inhibitors

Designing Hybrid Mesoporous Pr/Tannate-Inbuilt ZIF8-Decorated MoS2 as Novel Nanoreservoirs toward Smart pH-Triggered Anti-corrosion/Robust Thermomechanical Epoxy Nanocoatings

A Smart Anticorrosive Epoxy Coating Based on Graphene Oxide/Functional Mesoporous Silica Nanoparticles for Controlled Release of Corrosion Inhibitors

The preparation of cerium nitrate and attapulgite based superhydrophobic epoxy coatings for the corrosion protection of Q355 mild steel surface

Novel anticorrosive zinc phosphate coating for corrosion prevention of reinforced concrete