Abstract:Industrial-use VOx-based catalysts usually have a higher active temperature window (> 250-300°C), which becomes a “bottleneck” for the practical application of PCDD/Fs catalytic degradation technology. In this work, VOx-FeOx/TiO2 catalyst prepared via mechanochemically method was investigated for the catalytic removal of PCDD/Fs. The removal efficiency of 1,2-DCBz, pure PCDD/Fs gas generated in the lab, PCDD/Fs from actual flue gas, long-term were studied, and the degradation mechanism was explored using FTIR and TOFMS. The degradation efficiency of 1,2-DCBz and PCDD/Fs on VOx-FeOx/TiO2 were higher than that of VOx/TiO2 catalyst, and the optimal FeOx addition ratio was 3 wt.%. The characterization results show that the addition of FeOx can effectively improve the pore structure, surface acidity, and VOx dispersion of the catalyst, thus contributing to increasing the V5+ content and surface-active oxygen, which is conducive to the improvement of adsorption and redox performance of the catalyst. Under the actual MSWI (municipal solid waste incineration) flue gas, the PCDD/Fs removal efficiency over VTi-3Fe-MC maintained long-term stability, higher than 85% for 240 min. This result was not significantly reduced compared with the data obtained in the laboratory. According to the analysis results of intermediate products by FTIR and GC-TOFMS, it can be inferred that the epoxidation fracture of benzene ring is the rate-limiting step of dioxin catalytic degradation reaction. This work gives an in-depth view into the PCDD/Fs removal over VOx-FeOx/TiO2 catalysts and could provide guidelines for the rational design of reliable catalysts for industrial applications.

Enhancing Mechanisms of N-doped Biomass Carbon on the Vanadium-Based Catalyst for Furan Degradation at Low Temperature

Construction of N, O Co-Doped Carbon Anchored with Co Nanoparticles As Efficient Catalyst for Furfural Hydrodeoxygenation in Ethanol

Promoting Effect of FeOx Addition on the Mechanochemically Prepared Vanadium-Based Catalyst for Real PCDD/Fs Removal and Mechanism Insight

Ozone Assisted Oxidation of Gaseous PCDD/Fs over CNTs-containing Composite Catalysts at Low Temperature.

In-situ Fe–O Co-Doped Carbon Nitride Heterogenous Catalyst for Enhanced Photo-Fenton Oxidation Performance Towards Recalcitrant Organic Pollutants

Temporal Trends and Variation in Bronchoscopy Use for Acute Respiratory Failure in the United States

Enhanced H2O2 Utilization Efficiency in Fenton-like System for Degradation of Emerging Contaminants: Oxygen Vacancy-Mediated Activation of O2.

Selective Hydrogenation of Furfural to Furfuryl Alcohol Without External Hydrogen over N-doped Carbon Confined Co Catalysts

PCDD/F removal at low temperatures over vanadium-based catalyst: insight into the superiority of mechanochemical method

Catalytic decomposition of gaseous PCDD/Fs over V2O5/TiO2-CNTs catalyst: Effect of NO and NH3 addition.

Comparative Analyses of Catalytic Degradation of PCDD/Fs in the Laboratory Vs. Industrial Conditions

Comparative analyses of catalytic degradation of PCDD/Fs in the laboratory vs. industrial conditions.

MIL-47(V)-derived carbon-doped vanadium oxide for selective oxidation of 5-hydroxymethylfurfural to 2,5-diformylfuran

Facile synthesis of ammonium trivanadate(V)/nitrogen doped carbon composites with high catalytic activity for the selective oxidation of 5-hydroxymethylfurfural

Catalytic Destruction of PCDD/Fs over Vanadium Oxide-Based Catalysts.

Catalytic Decomposition of PCDD/Fs over Nano-TiO2 Based V2O5/CeO2 Catalyst at Low Temperature

Low temperature destruction of PCDD/Fs by catalysis coupled with activated carbon

Low Temperature Degradation of Polychlorinated Dibenzo-P-dioxins and Dibenzofurans over a VOx-CeOx/TiO2 Catalyst with Addition of Ozone.

New mechanistic insight into catalytic decomposition of dioxins over MnOx-CeO2/TiO2 catalysts: A combined experimental and density functional theory study

Renewable biomass-derived, P-doped granular activated carbon for efficient oxidation of 5-hydroxymethylfurfural to 2,5-diformylfuran: Insights into the crucial role of P and N functionality

Low Temperature Oxidation of PCDD/Fs by TiO2‐based V2O5/WO3 Catalyst