Abstract:Aluminum particles have the problems of difficult ignition, easy agglomeration, incomplete combustion, etc. Therefore, it is of great scientific significance and engineering value to find ways to improve the ignition and combustion performance of aluminum particles in order to promote the full release of energy of aluminum particles. In this paper, spherical nano-sized ferric oxide (nFe 2 O 3 ) and ammonium perchlorate (AP), a commonly used oxidizer in propellants, were used to synergistically improve the ignition and combustion performance of aluminum particles. AP modified the aluminum particles by both mixing and coating methods, respectively. On the basis of coating AP, nFe 2 O 3 was added in order to further enhance the ignition and combustion performance of the aluminum particles. Scanning electron microscope, laser particle size analyzer, thermal analysis system and laser ignition experiment system were used to test the physicochemical properties and ignition combustion performance of different samples. The results showed that AP and nFe 2 O 3 could be coated relatively uniformly on the surface of aluminum particles using the recrystallization method. The thermal reaction behavior of the samples showed that coating was beneficial to the decomposition of AP compared with mixing, and the addition of nFe 2 O 3 could further improve the decomposition efficiency of AP. Ignition and combustion experiments showed that coating AP was more conducive to improving the ignition and combustion performance of aluminum particles than mixing AP, and the addition of nFe 2 O 3 could further significantly enhance the combustion intensity and flame propagation speed of the sample. However, the addition of nFe 2 O 3 increased the ignition delay time of the sample, which may be related to the cold agglomeration phenomenon caused by the nanoparticles. The microscopic combustion flame morphology of different samples showed that coating AP and the introduction of nFe 2 O 3 could significantly reduce the agglomeration phenomenon of aluminum particles. Overall, coating AP reduces the distance between the aluminum particles and the oxidizer, thus significantly improving the ignition and combustion performance of the aluminum particles. The addition of nFe 2 O 3 can further improve the combustion performance of aluminum particles, but at the same time, it also increases the ignition delay time. Hence, the cold agglomeration problem caused by nanoparticles should be fully considered when nFe 2 O 3 is used to improve the ignition and combustion performance of aluminum particles.

Self-assembly of Composite Salts Induced Uniform, Ammonium Perchlorate-Catalytic, Ignitable and Energetic Coating on Aluminum Fuels

Construction of Hydrophobic Ammonium Perchlorate with Synergistic Catalytic Effect Based on Supramolecular Self-Assembly for Synchronously Catalyzing the Thermal Decomposition of Ammonium Perchlorate and the Combustion of Aluminum

Micro-aluminum powder with bi- or tri-component alloy coating as a promising catalyst: Boosting pyrolysis and combustion of ammonium perchlorate

Novel aluminum-based fuel: Facile preparation to improve thermal reactions

Synthesis of an Fe/Al composite nanocatalyst with improved catalytic stability for ammonium perchlorate decomposition

AP and Nfe 2 O 3 Synergistically Improve the Ignition and Combustion Performance of Aluminum Particles

AP and nFe2O3 synergistically improve the ignition and combustion performance of aluminum particles

Enhanced thermal, safety and anti-hygroscopicity performance of core-shell ammonium perchlorate with double coating layer

Combustion and heat release characteristics of micron aluminum with extremely large specific surface area obtained by L-malic acid surface corrosion

Ammonium perchlorate@graphene oxide/Cu-MOF composites for efficiently catalyzing the thermal decomposition of ammonium perchlorate

Facile Grinding Method for Preparing Nano-Cu-Cr-Fe Composite Metal Oxides with Enhanced Catalytic Activity for Thermal Decomposition of Ammonium Perchlorate

Establishing the interface layer on the aluminum surface through the self-assembly of tannic acid (TA): Improving the ignition and combustion properties of aluminum

Ignition and combustion of Al and ammonium perchlorate-coated Al particles in a double oxidizing air–H2O–Ar atmosphere

The catalytic thermal decomposition of ammonium perchlorate on CuMxOy (M = Fe, Ni, Co and Zn) catalysts and their applications in solid propellant

A study on modification of aluminum powder by ammonium perchlorate and glycidyl azide polymer to improve its combustion

One-step Synthesis of Ferrocenyl Glycidyl Ethers As Combustion Catalysts for the Thermal Decomposition of Ammonium Perchlorate

Preparation and characterization of composite particles of Al/ammonium perchlorate

New Insights into the Catalytic Decomposition of Ammonium Perchlorate and Decomposition Mechanism by Nano‐CuO Dispersed in Graphite‐Carbon Nitride Nanosheet Composites

The catalytic thermal decomposition of ammonium perchlorate on CuM x O y (M = Fe, Ni, Co and Zn) catalysts and their applications in solid propellant

Enhancing the Ignition and Combustion Performance of Aluminum by Surface Modification: Tannic Acid and Tea Polyphenols

Iron/aluminum nanocomposites prepared by one-step reduction method and their effects on thermal decomposition of AP and AN