Micro morphology and properties of tribological action for shell in Cyclina sinensis
Ma Yunhai,Lin Fudong,Yan Zhifeng,Zhuang Jian,Wang Zhiqin,Deng Zhihua,Tong Jin
DOI: https://doi.org/10.3969/j.issn.1002-6819.2013.18.036
2013-01-01
Abstract:Shells of Cyclina sinensis have excellent mechanical properties, and they have become a hot research topic for bionic design and materials development. Cyclina sinensis shells in the City of Yingkou, Liaoning Province were our research subject. The micromorphology of different layers of Cyclina sinensis shells was observed by using JSM-6700F cold field scanning electron microscope (SEM), and it was shown that the surface of the periostracum was comparatively smooth, and its back was covered by a large number of irregular, spherical particles. There are lots of holes on the surface of the prismatic layer, and the secreted mucus of Cyclina sinensis shells arrives at the surface of the periostracum through those holes. When the particle size and pore size of the prismatic surface coincide was in the same scope with good chimeric, periostracum and prismatic layers were closely together under secreted mucus. Tribological properties of the Cyclina sinensis shell was studied by using UMT micro-friction and a wear-testing machine. The experiment showed that the relative order of influence on the friction coefficient is sand paper, normal load, time, and sliding speed;the relative order of influence on the wear rate is sand paper, time, sliding speed, and normal load. The smallest wear rate was observed when the time was 5 min, the normal load was 20 N, the sliding speed was 0.188 m/s, and the sandpaper specification was 1000 meshes. Under those conditions the wear performance of Cyclina sinensis shell was best. According to the results of an orthogonal experiment, under the conditions of friction time 1000 s, sliding speed 0.188 m/s, and sandpaper specification of 1000 meshes, sample data and worn surface micromorphology were analyzed under the conditions of two normal loads, 20 N and 25 N. When the normal load was 20 N, in the early portion of the experiment the Cyclina sinensis shell had a larger friction coefficient, and the periostracum and sandpaper began to contact with each other. The periostracum was worn away after 25 s, the prismatic layer and sandpaper began to contact with each other, so the friction coefficient briefly decreased, after which the friction coefficient began to increase again, reaching a stable value at about 300 s. When the normal load was 20 N at the beginning of the friction surface the complex microstructure under high load was damaged because of excessive pressure. Micro morphology of worn surface for shells of Cyclina sinensis was observed using JSM-6360LV cold field scanning electron microscope (SEM), the major worn mechanism for shell of Cyclina sinensis were abrasive wear and mild delamination wear under low test load condition, as well as abrasive wear and serious delamination wear under higher test load condition.