Effect of Green Bactericidal Corrosion Inhibitor on Corrosion Behavior of Carbon Steel with Different Surface Roughness

XU Cong-min,YANG Xing,ZHU Wen-sheng,GAO Hao-ran,YAO Pan,ZHANG Jin-rui

DOI: https://doi.org/10.16490/j.cnki.issn.1001-3660.2023.11.025

2023-01-01

Surface Technology

Abstract:At present， as microbial corrosion has gradually become an important form of pipeline material destruction， and some traditional chemical methods to mitigate corrosion will bring various negative effects such as environmental pollution. From the angle of green environmental protection， the new green bactericidal corrosion inhibitor of our research group has been selected， and the effect of the green bactericidal corrosion inhibitor on the corrosion process of carbon steel in the sulfate-reducing bacteria （SRB） and iron-oxidizing bacteria （IOB） mixed bacteria on the different surface roughness is studied. The objective is to reveal the effect of green bactericidal corrosion inhibitor on the bactericidal corrosion inhibition behavior and law of SRB+IOB biofilm on carbon steel surface with different roughness. Weight loss experiments， surface analysis and electrochemical tests were used to investigate the bactericidal behaviour and the corrosion inhibition effect on 20# carbon steel at different roughnesses （240#， 600# and 1200#） with the addition of green bactericidal corrosion inhibitor on mixed bacteria， as well as the mechanism of action of D-tyrosine to decompose and inhibit biofilm. The thickness of the corrosion product layer， the size and depth of pitting pit on the surface of 20# steel sample decreased with the decrease of surface roughness and the addition of bactericidal inhibitor. In the case of no added bactericidal corrosion inhibitor， with the surface roughness decreasing from 240# to 1200#， the annual corrosion depth of carbon steel was reduced from 0.186 （mm/a） to 0.157 （mm/a） by 15.6%， and the self-corrosion current density i corr was reduced from 20.5×10 -6 (A/cm 2 ) to 6.93×10 -6 (A/cm 2 ) by 66.2%; For 240# surface roughness， the annual corrosion depth of carbon steel was reduced from 0.186 （mm/a） without bactericide to 0.116 （mm/a） with bactericide by 37.6%; the i corr was reduced from 20.5×10 -6 (A/cm 2 ) to 11.8×10 -6 (A/cm 2 ) by 42.4%. On the one hand， the rougher the surface of carbon steel， the deeper the surface groove will be， which is easy to produce stress concentration， and cause local defects in the oxide film on the metal surface. The defective part is used as the anode， and the surrounding part is used as the cathode， resulting in occluded cells， gradually forming pitting nuclei， causing surface damage. However， with the reduction of surface roughness， the carbon steel surface tends to be more smooth， the stress concentration is reduced. It is difficult for the carbon steel surface to gather sulfide， mineralized substances and corrosive anions in mixed bacteria. H + is difficult to combine with anions to form an acidic environment， thus not easy to generate oxygen concentration difference cell， slow down the transformation from uniform corrosion to local corrosion， and reduce the probability of pitting corrosion. On the other hand， aerobic IOB bacteria can utilize O 2 to oxidize Fe 2+ to Fe 3+ in water and form an oxide film on the surface of the sample， Fe 2+ as carrier， terminal receptor is O 2 ， which will accelerate the reaction with iron， At the same time， the oxide film blocks the O 2 in the solution， and provides anaerobic space for SRB anaerobic bacteria， so that SRB reduces SO 4 2- to HS - ， and Fe 2+ and S 2- can combine to produce FeS， which is more likely to aggravate corrosion; However， the addition of D-tyrosine can effectively decompose and inhibit biofilm， make bacteria change from fixed state to floating state， reduce the generation of EPS， reduce the complexation of Fe 2+ ， and reduce the synergy of IOB and SRB；at the same time， the green bactericidal and corrosion inhibitor also changes the cell structure in the cell membrane， destroys the bacterial cell membrane， cell wall， and cell protein， and also destroys the oxygen concentration environment， thus enhances the bactericidal and corrosion inhibition effect.