Abstract:The influence of external potentials on the electrochemical corrosion characteristics and pitting resistance of Low Carbon High Chromium (H), Duplex (D), Corrosion Resistant (R) duplex stainless steel after film formation was investigated by techniques such as dynamic potential scanning, constant potential polarization, Electrochemical Impedance Spectroscopy (EIS), conjunction with Scanning Electron Microscope (SEM) and Energy Dispersive Spectroscopy (EDS) analysis, were used to examine the effects of passivation potential and over-passivation potential on the pitting resistance of HDR duplex stainless steel, compared with naturally film-formed HDR corrosion resistance. Results show that in a 3.5% NaCl solution, the passivation range of HDR duplex stainless steel is 0~1.0 V, with certain current fluctuation appearing in the unstable pitting region around 1.0 V. As the film formation potential increases, the impedance first increases then decreases, and the carrier concentration first decreases then increases. At 0.9 V, the impedance is at its maximum, the carrier concentration is at its minimum, and the corrosion resistance is the best; at 1.2 V, the impedance is at its minimum, the carrier concentration is at its maximum, and the corrosion resistance is the worst; the natural film formation sample falls between 0.1 V and 0.7 V. After pitting tests, pitting mainly occurs at the ferrite structure and its boundaries for the naturally film-formed and film-formed potentials below 1.0 V samples, but pitting mainly occurs at the austenite structure and its boundaries in the 1.2 V film-formed sample, indicating a reversal of corrosion in the structural pitting. The sample with the film formation potential of 0.1 V developed many small pits on the surface after pitting test, which is related to the oxidation of Mo.

The Formation of Pitting under Dynamic Dc Interference: Corrosion Product Film Defects or Passive Film Induction

Localized corrosion: Passive film breakdown vs. Pit growth stability, Part VI: Pit dissolution kinetics of different alloys and a model for pitting and repassivation potentials

Molecular Dynamics Simulation of Reinforcing Steel Corrosion when Subjected to Both Chloride Attack and Mechanical Loading

Studies on Pitting Corrosion of Al-Cu-Li Alloys Part III: Passivation Kinetics of AA2098-T851 Based on the Point Defect Model

Simulation Investigation on Environment-Induced Pitting Corrosion on the Metal Surface

Comprehending the coupled effect of multiple microstructure defects on the passive film features and pitting behavior of UNS S32101 in simulated seawater

Direct observation of pitting corrosion evolutions on carbon steel surfaces at the nano-to-micro- scales

Structure and Composition of the Passive Film Studied Using a Combination of X-Ray Photoelectron Spectroscopy, Secondary Ion Mass Spectrometry, and Scanning Transmission Electron Microscopy

Studies on Pitting Corrosion of Al-Cu-Li Alloys Part II: Breakdown Potential and Pit Initiation

An Investigation on Corrosion Behavior and Mechanism of CoCrFeNi HEA in NaCl Solution under Direct Current Interference

On the origin of passive film breakdown and metastable pitting for stainless steel 316L

A microstructure-sensitive electro-chemo-mechanical phase-field model of pitting and stress corrosion cracking

The corrosion deterioration of reinforced passivation Film: The impact of defects

Phase-field model of pitting corrosion kinetics in metallic materials

New diffusive interface model for pitting corrosion

Initiation and propagation of pitting and crevice corrosion of hydrogen-containing passive films on X70 micro-alloyed steel

Investigations on the passive and pitting behaviors of the multiphase stainless steel in chlorine atmosphere

A review of passivity breakdown on metal surfaces: influence of chloride- and sulfide-ion concentrations, temperature, and pH

Study on pitting behavior of HDR duplex stainless steel at different film-forming potentials

Systematic Insight into Chloride Concentration, Applied Potential and Time Effect on the Passive Film of Cu-Zn-Ni Ternary Alloy in Alkaline Solution

Metastable Pitting and Its Correlation with Electronic Properties of Passive Films on Sn–xZn Solder Alloys