Abstract:Generally, film dielectric materials often exhibit size-dependent structure and electric properties.In this work, we demonstrate a similar behavior in bulk Na0.5Bi0.5TiO3(NBT)-based polycrystalline ceramics.According to the results from X-ray diffraction, the (Na0.5Bi0.5)0.92Ba0.08Ti0.99Mg0.01O2.99(NBT8M1.0)ceramic showed a complex structure that consists of rhombohedral, tetragonal and cubic symmetries.We found, when decreasing the thickness of a ϕ 10 mm NBT8M1.0 ceramic from 1230 μm to 230 μm, the ceramic showed increased content of cubic symmetry (CC) from 28% to 56%.Meanwhile, the piezoelectric response (d33) increased from 107 pC/N to 134 pC/N and the depolarization temperature (Td) decreased from 170 ℃ to 142 ℃.Similarly, when decreasing the diameter of a 1 mm thick NBT8M1.0 ceramic from ϕ 22 mm to ϕ 6 mm, the ceramic showed increased CC from 18% to 44%.Meanwhile, the d33 increased from 125 pC/N to 135 pC/N and the Td decreased from 165 ℃ to 156 ℃.The origin of size-dependent structure and properties in macroscopic size range of NBT8M1.0 ceramics were further studied by investigating the difference of the size-dependence between the ceramics sintered from green bodies prepared by uniaxial pressing and isostatic pressing.The results demonstrated that the size-dependent structure and properties of NBT-based polycrystalline ceramics are closely related to the residual stress from the inhomogeneous densification during sintering process, as a result of the inhomogeneous density distribution in the pressed green body.

Size Dependent Structures and Properties of Na0.5Bi0.5TiO3-Based Ceramics for Piezoelectric Sensors