Metal–Organic Framework-Derived Porous NiCo-Layered Double Hydroxide@MnO 2 Hierarchical Nanostructures as Catalytic Cathodes for Long-Life Li–O 2 Batteries
Mingjie Ding,Peng Wang,Zhiwei Zhang,Longwei Yin
DOI: https://doi.org/10.1021/acsaem.0c01626
IF: 6.4
2020-12-31
ACS Applied Energy Materials
Abstract:The commercial application of lithium–oxygen (Li–O<sub>2</sub>) batteries has been seriously hindered by their large overpotential and inferior cycling performance caused by the insoluble and insulated traits of the discharge product, Li<sub>2</sub>O<sub>2</sub>. Herein, hierarchical hollow NiCo-LDH/MnO<sub>2</sub> hybrid nanostructures derived from metal–organic frameworks (MOFs) are successfully constructed as cathodes for Li–O<sub>2</sub> batteries to fundamentally improve the decomposition kinetics of Li<sub>2</sub>O<sub>2</sub>. The hollow NiCo-LDH/MnO<sub>2</sub> nanostructures assembled by hollow NiCo-LDH and MnO<sub>2</sub> nanosheets possess a highly special surface area, abundant open active sites, and a fast diffusion path for Li<sup>+</sup> and oxygen species. As expected, accelerated sluggish oxygen reduction reaction/oxygen evolution reaction kinetics and reduced charge/discharge overpotentials can be obtained. The toroidal Li<sub>2</sub>O<sub>2</sub> assembled by nanoflakes formed on the surface of the cathode can be conducive to form a low-impedance Li<sub>2</sub>O<sub>2</sub>/cathode contact interface to achieve the reversible formation and decomposition of Li<sub>2</sub>O<sub>2</sub>. The Li–O<sub>2</sub> battery based on the NiCo-LDH/MnO<sub>2</sub> cathode shows a high charge/discharge specific capacity of 13,380 mA h g<sup>–1</sup> at 100 mA g<sup>–1</sup> and a continuous cycling stability for 162 cycles at a fixed capacity of 500 mAh g<sup>–1</sup> as well as a low overpotential of 0.63 V. Moreover, the application of MOF-derived porous hierarchical nanostructures expands the selection range of electrocatalysts and offers a new idea of structure design for Li–O<sub>2</sub> batteries.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsaem.0c01626?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsaem.0c01626</a>.Experimental details, SEM images, TEM images, N<sub>2</sub> adsorption/desorption isotherms, EDS image, survey spectrum and electrochemical analysis (discharge/charge curves, Nyquist plots, rate performance, and cycling stability performance), contents of MnO<sub>2</sub> in the NiCo <sub>2</sub>-X sample calculated from XPS, comparison of the performance of the NiCo <sub>2</sub>-X nanocomposite electrodes, and SEM images and XPS spectra of electrodes after discharge and charge (<a class="ext-link" href="/doi/suppl/10.1021/acsaem.0c01626/suppl_file/ae0c01626_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.
materials science, multidisciplinary,chemistry, physical,energy & fuels