Efficient deep-red luminescence with high colour purity from Mn4+-doped ZnAl2O4 nanophosphor
Vikas,Vikas Lahariya,Rajnee Yadav,Raunak Kumar Tamrakar,Aditya Yadav,Govind Gupta,Anit Dawar
DOI: https://doi.org/10.1007/s10853-023-08920-7
IF: 4.5
2023-09-27
Journal of Materials Science
Abstract:This work presents a highly intense deep-red luminescence (710–748 nm) from non-rare earth (Mn 4+ )-doped zinc aluminate (ZnAl 2 O 4 ) nanophosphor. The effect of different concentration of Mn (0.3–4%) on structural, morphological, optical properties and luminescence behaviour of ZnAl 2 O 4 nanocrystals are investigated. The Mn-doped ZnAl 2 O 4 nanocrystals were prepared by microwave combustion method with annealing of the sample at 900 °C and characterized by different techniques. The pure spinel structure with mean crystallite size 12–35 nm is found. Further, the estimated value of optical band gap E g (4.5–2.25 eV) is reduced with increasing Mn concentration, due to creation of sub-bands between valence and conduction gap. From photoluminescence (PL) study, PL excitation bands at 353 nm, 375 nm in ultraviolet region referring to 4 A 2g → 4 T 1g , and bands at 425 nm, 450 nm in visible region referring to 4 A 2g → 2 T 2g and 4 A 2g → 4 T 2g transitions, respectively, are obtained. PL emission spectra exhibited broad emission band ~ 440–510 nm attributed to host zinc aluminate nanocrystals along with highly intense emission in the deep-red region ~ 710–748 nm accredited to transition from 2 E g → 4 A 2g of Mn 4+ dopant ions. Among all concentration, highly intense, 92% colour pure prominent deep-red band at ~ 710 nm is observed for 0.5% Mn 4+ -doped ZnAl 2 O 4 nanocrystals. It is found that Mn 4+ emission centre emits out the deep-red emission and the strong crystal field of Mn 4+ in host enhanced the emission. The critical distance, crystal field strength and Racah parameters have been calculated. The possible electronic transitions explained by T–S (Tanabe–Sugano) diagram and concentration quenching mechanism are discussed. The 6.42 ms mean lifetime was found for 0.5% Mn-doped zinc aluminate from PL decay plot. The obtained parameters suggested the potential applications of Mn 4+ -doped zinc aluminate deep-red nanophosphor for display applications, WLED and for bio-imaging.
materials science, multidisciplinary