Abstract:In the process of promoting the commercialization of proton exchange membrane fuel cells, the long-term durability of the fuel cell has become a key consideration. While existing durability tests are critical for assessing cell performance, they are often time-consuming and do not quickly reflect the impact of actual operating conditions on the cell. In this study, improved testing protocols were utilized to solve this problem, which is designed to shorten the testing cycle and evaluate the degradation of the cell performance under real operating conditions more efficiently. Accelerated durability analysis for evaluating the MEA lifetime and performance decay process was carried out through two testing protocols—open circuit voltage (OCV)-based accelerated durability testing (ADT) and relative humidity (RH) cycling-based ADT. OCV-based ADT revealed that degradation owes to a combined mechanical and chemical process. RH cycling-based ADT shows that degradation comes from a mainly mechanical process. In situ fluoride release rate technology was employed to elucidate the degradation of the proton exchange membrane during the ADT. It was found that the proton exchange membrane suffered more serious damage under OCV-based ADT. The loss of F- after the durability test was up to 3.50 × 10−4 mol/L, which was 4.3 times that of the RH cycling-based ADT. In addition, the RH cycling-based ADT had a significant effect on the catalyst layer, and the electrochemically active surface area decreased by 48.6% at the end of the ADT. Moreover, it was observed that the agglomeration of the catalysts was more obvious than that of OCV-based ADT by transmission electron microscopy. It is worth noting that both testing protocols have no obvious influence on the gas diffusion layer, and the contact angle of gas diffusion layers does not change significantly. These findings contribute to understanding the degradation behavior of proton exchange membrane fuel cells under different working conditions, and also provide a scientific basis for developing more effective testing protocols.

Understanding of Free Radical Scavengers Used in Highly Durable Proton Exchange Membranes

A Highly Durable Quercetin-Based Proton Exchange Membrane for Fuel Cells

Ceria Nanorods As Highly Stable Free Radical Scavengers for Highly Durable Proton Exchange Membranes

Expanded polytetrafluoroethylene functionalized with free radical scavengers and hydrophilic groups for superior chemical stability of proton exchange membranes

Assessing Free Radical Scavenging Activity of Various Cerium Materials for Proton Exchange Membrane Fuel Cells Using Fluorescence Spectroscopy Presentation Format

Durability enhancement of proton exchange membrane fuel cells by ferrocyanide or ferricyanide additives

Design of proton exchange membranes with high durability for fuel cells: From the perspective of machine learning

Double-Layer Expanded Polytetrafluoroethylene Reinforced Membranes with Cerium Oxide Radical Scavengers for Highly Stable Proton Exchange Membrane Fuel Cells

Grafting free radical scavengers onto polyarylethersulfone backbones for superior chemical stability of high temperature polymer membrane electrolytes

Durability improvement of proton exchange membrane fuel cells by doping silica‒ferrocyanide antioxidant

Key Components Degradation in Proton Exchange Membrane Fuel Cells: Unraveling Mechanisms through Accelerated Durability Testing

Enhanced radical scavenging performance of Pt@CeO2 via strong metal-support interaction effect for improving durability of proton exchange membrane fuel cell

Performance of functionalized graphene oxide with organic radical scavengers in proton exchange membranes

Mechanical Failure and Mitigation Strategies for the Membrane in a Proton Exchange Membrane Fuel Cell

Evaluating the Durability of Perfluorosulfonic Acid Membranes in Fuel Cells Using Combined Open-Circuit Voltage-Accelerated Stability Testing

Durability Improvement for Eptfe Reinforced Perfluorosulfonic Acid Membranes by Natural Organic Free Radical Scavengers

Advanced proton exchange membrane prepared from N-heterocyclic poly(aryl ether ketone)s with pendant benzenesulfonic moieties and performing enhanced radical tolerance and fuel cell properties

Research Progress of Proton Exchange Membrane Failure and Mitigation Strategies

Influence of structure construction on water uptake, swelling, and oxidation stability of proton exchange membranes

A paradigm shift for a new class of proton exchange membranes with ferrocyanide proton-conducting groups providing enhanced oxidative stability

The review of the degradation mechanism of the catalyst layer of membrane electrode assembly in the proton exchange membrane fuel cell