Broadly Tunable Emission from CaMoO ₄ :Bi Phosphor Based on Locally Modifying the Microenvironment Around Bi ³⁺ Ions

Fengwen Kang,Mingying Peng,Shanhui Xu,Zhijun Ma,Guoping Dong,Jianrong Qiu

DOI: https://doi.org/10.1002/ejic.201301481

IF: 2.551

2014-01-01

European Journal of Inorganic Chemistry

Abstract:Abstract The trivalent green element of bismuth, when doped into different compounds, can produce multiple emissions in ultraviolet, blue, green or even yellow spectral regimes. The emission adjustability comes from the susceptibility of bismuth naked 6s electrons to the crystal field particularly surrounding Bi 3+ . However, this has never been observed in a single compound. In this work, we report that broadly tunable bismuth emission indeed occurs even within the same host (CaMoO 4 ) when the local microenvironment around Bi 3+ is modified by intentional introduction of alkali ions. As the radius of the selected alkali ion decreases, the emission regularly blue‐shifts from 586 to 554 nm, and its intensity is enhanced greatly. For instance, the integrated intensity for the Li + and Bi 3+ codoped sample is 4.46 times stronger than the Bi 3+ single‐doped sample upon excitation at 300 nm. Low‐temperature photoluminescence spectra surprisingly reveal that energy transfer can partially take place from the MoO 4 2– group to Bi 3+ at lower temperature when excited into the charge transfer state of the MoO 4 2– group, however, this does not occur at higher temperature. The mechanism needs further study. Dynamic luminescence analysis between 10 and 300 K implies a population dependence of the excited states 3 P 0 and 3 P 1 on temperature that is responsible for the evolution of the Bi 3+ emission lifetime with temperature.