Effect of Twin Content on Sulfur Corrosion Resistance of Copper Windings

Huiying Xiang,Yuan,Tao Zhu,Xu Dai,Ruijin Liao

DOI: https://doi.org/10.23919/iseim60444.2023.10329170

2023-01-01

Abstract:Recently, the oil-sulfur corrosion of copper winding in transformer has been widely concerned at home and abroad. However, most of the solutions to this phenomenon focus on insulating oil, mainly including strict acceptance of new oil, addition of metal passivator, etc., and the research on copper winding itself is lacking. Herein, grain boundary engineering was used to treat copper windings, and the effect of twin content on sulfur corrosion resistance of copper windings was researched. Copper windings with different twin content (18.2, 41.2 and 61.6 % ) were obtained by adjusting the deformation of copper. According to IEC 62535 standard, the oil-sulfur corrosion test was carried out. The results show that the corrosion product deposits on copper windings and insulation paper decrease as the twin content increases. Moreover, the large twin content can improve the electrical performance of the insulating oil and insulating paper. The electrochemical polarization curve of the copper windings was measured. With the increase of twin content, the corrosion potential shifts positively and the corrosion current density decreases. This explains the mechanism that increasing the twin content improves the corrosion resistance of copper windings. This work provides useful information for suppressing oil sulfur corrosion in transformers.