Evolution of Temperature-Induced Isostructural Phase Transition in a Newly Grown Layered FeTe 2 Single Crystal
Hao Wu,Zhenjie Feng,Arnab Pal,Hongliang Dong,Chao Jing,Ke Wang,Shihui Zhang,Wen Deng,Shujia Li,Jiajia Feng,Jiafeng Chen,Yanhong Chen,Jingying Si,Jun-Yi Ge,Shixun Cao,Bin Chen,Jincang Zhang
DOI: https://doi.org/10.1021/acs.chemmater.1c00467
IF: 10.508
2021-06-18
Chemistry of Materials
Abstract:Layered FeTe<sub>2</sub> (l<i>-</i>FeTe<sub>2</sub>) was supposed to be one of the most important compounds in the family of two-dimensional transition-metal dichalcogenides (2D TMDs) owing to the importance of an iron element and its predicted novel physical phenomena. However, 2D layered FeTe<sub>2</sub> is rarely reported because of its tendency to be stabilized in three-dimensional marcasite phase structures. Here, we report, for the first time, a pure and large-size l-FeTe<sub>2</sub> single crystal synthesized successfully in a <i>P</i>3̅<i>m</i>1 hexagonal space group using a solid-state reaction method. Thermoanalysis and X-ray diffraction (XRD) data after annealing at different temperatures indicate that l<i>-</i>FeTe<sub>2</sub> is a metastable material. The results of electrical transport, magnetization, and in situ low-temperature XRD measurements confirm that l-FeTe<sub>2</sub> undergoes a first-order isostructural phase transition from 120 to 150 K, and we established a detailed correlation among these properties of l-FeTe<sub>2</sub>. l-FeTe<sub>2</sub> transforms from an insulating to metallic state at 120 K where the phase transition completes. In addition, the Shubnikov–de Haas (SdH) oscillation phenomenon is observed under a high magnetic field at 4 K.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acs.chemmater.1c00467?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acs.chemmater.1c00467</a>.l-FeTe<sub>2</sub> single crystal dissociated along the <i>a–b</i> direction and the location of point data and mapping data collected on the (001) face of EDS (Figure S1); the result of EDS analysis of Fe and Te elemental compositions at each point and their average on the l-FeTe<sub>2</sub> single crystal, which is shown in <a class="ext-link" href="/doi/suppl/10.1021/acs.chemmater.1c00467/suppl_file/cm1c00467_si_001.pdf">Figure S1</a> (Table 1); the electrical transport measurements under high pressure in diamond anvil cells from 0.66 to 10.2 GPa (Figure S2); the field dependence of magnetization (<i>M</i>–<i>H</i>) at different temperatures with the H ⊥ <i>a–b</i> plane (Figure S3); the experimental MR data and the fitted SdH oscillation curve at 2 K, which indicates that the SdH oscillation can be observed at a lower temperature (Figure S4); the Raman spectra of l-FeTe<sub>2</sub> at various temperatures from 100 to 250 K (Figure S5); and the list of the calculated lattice constants and the peak positions and FWHM of (004) characteristic peaks of l-FeTe<sub>2</sub> under different low temperatures (Tables S2 and S3) (<a class="ext-link" href="/doi/suppl/10.1021/acs.chemmater.1c00467/suppl_file/cm1c00467_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.
materials science, multidisciplinary,chemistry, physical