Preparation of Semiconductor ZnS Nanoparticles with Microwave Irradiation

Xin‐Hao Li

2002-01-01

Abstract:By means of microwave irradiation, ZnS nanoparticles in size of ca. 3 nm were prepared by a very simple fast reaction between zinc acetate and thioacetamide (TAA) in formaldehyde solution. The nanoparticlec were characterized by XRD, TEM and UV reflectance spectrum.

What problem does this paper attempt to address?

Preparation of CdS and ZnS nanoparticles using microwave irradiation

Junjie Zhu,Miaogao Zhou,Jinzhong Xu,Xuehong Liao

DOI: https://doi.org/10.1016/S0167-577X(00)00206-8

IF: 3

2001-01-01

Materials Letters

Abstract:Nanoparticles of CdS, ZnS have been prepared by a very simple fast reaction between CdCl2 or Zn(Ac)2 and thioacetamide in aqueous solution using microwave irradiation. The nanoparticles were characterized by X-ray diffraction (XRD), transmission electron microscopy (TEM), reflectance and photoluminescence spectra. The sizes of the sample as prepared were calculated by Debye–Scherrer formula according to XRD spectra to be about 9 and 3 nm for CdS and ZnS, respectively. Similar results can also been obtained in the TEM images.
Preparation of Zns Nanoparticles by Ultrasonic Radiation Method

J.F. Xu,W. Ji,J.Y. Lin,S.H. Tang,Y.W. Du

DOI: https://doi.org/10.1007/s003390050725

1998-01-01

Abstract:S solution. ZnS nanoparticles were synthesized under ultrasonic radiation. They were studied by X-ray diffraction (XRD), transmission electron microscopy (TEM), UV spectrophotometry, and X-rayphotoelectron spectrometry (XPS). XRD revealed that the ZnS nanoparticles prepared have a zincblende structure. TEM observations showed that the ZnS nanoparticles are in a spherical form with an average diameter of 40 nm. XPS results proved that, for our sample, the binding energies of Zn 2p and S 2p are the same as those of bulk single-crystal, but the full widths at half maximum of the XPS peaks are larger than those of bulk single-crystal.
Formation of Monodispersed Pvp-Capped Zns and Cds Nanocrystals under Microwave Irradiation

R He,XF Qian,J Yin,HA Xi,LJ Bian,ZK Zhu

DOI: https://doi.org/10.1016/s0927-7757(03)00072-4

2003-01-01

Abstract:Poly (N-vinyl-2-pyrrolidone) (PVP)-capped ZnS, CdS nanoparticles were prepared by a microwave method from Zn(Ac)2 or Cd(Ac)2 and thiourea in N,N-dimethylformamide (DMF) solution. The reaction process was monitored by the temporal evolution of the absorption spectrum. With PVP as stabilizer, monodispersed semiconductor nanoparticles, which showed high quantum size effect, have been obtained. Further study showed that the microwave irradiation could influence selectively the nucleation and growing rates of different semiconductor nanoparticles.
γ-Irradiation preparation and characterization of nanocrystalline ZnS

Zhengping Qiao,Yi Xie,Yitai Qian,Yingjie Zhu

DOI: https://doi.org/10.1016/S0254-0584(99)00151-0

IF: 4.778

2000-01-01

Materials Chemistry and Physics

Abstract:The γ-irradiation method was used successfully to prepare nanocrystalline ZnS in sphalerite structure at room temperature. Sodium thiosulfate, thiourea and mercaptoethanol were used as sulfur sources. The products obtained from irradiated solutions containing zinc ions and different sulfur sources are all sphalerite phase. The TEM images indicate that the product from mercaptoethanol is in best dispersion, and that from sodium thiosulfate aggregates most heavily. The possible mechanisms of the formation of zinc sulfide in different systems are proposed.
Microwave Synthesis Of Nanocrystalline Metal Sulfides In Formaldehyde Solution

Xh Liao,Jj Zhu,Hy Chen

DOI: https://doi.org/10.1016/S0921-5107(01)00647-X

2001-01-01

Abstract:Nanocrystalline metal (Cu, Hg, Zn, Pi, Ph) sulfides with different shapes and different particle sizes have been successfully prepared in a formaldehyde solution of metal salt and thioacetamide by microwave irradiation. Powder X-ray diffraction patterns indicated that the products were pure orthorhombic Bi2S3 phase, cubic phase HgS, hexagonal phase CuS, cubic phase ZnS, cubic phase PbS, respectively. The products were also characterized by transmission electron microscopy. Ultraviolet reflection spectrum clearly indicates the presence of quantum size effects in ZnS. (C) 2001 Elsevier Science B.V. All rights reserved.
Microwave Assisted Preparation of CdSe , PbSe , and Cu 2x Se Nanoparticles

JJ Zhu,O Palchik,SG Chen,A Gedanken

DOI: https://doi.org/10.1021/jp001488t

2001-01-01

ChemInform

Abstract:Nanoparticles of various dimensions of II-VI binary chalcogenides CdSe, PbSe, and Cu2-xSe, have been prepared by a very simple fast reaction between acetates or sulfates of Cd, Pb, and Cu and Na2SeSO3 in the presence of complexating agents, using microwave irradiation. The nanoparticles were analyzed by X-ray diffraction (XRD), electron microscopy (TEM) and X-ray photoelectron spectroscopy (XPS).
Studies of synthesis and optical properties of ZnS nanocrystals

Min Zhong,Gaorong Han,Hongliang Ge

DOI: https://doi.org/10.3321/j.issn:1002-185x.2007.02.026

2007-01-01

Rare Metal Materials and Engineering

Abstract:ZnS nanoparticles and one-dimensional nanocrystals were obtained by in-situ synthesis in Aa-AMPS-hT ternary periodic copolymer by ion complexometry and self-assembly method. The micro-morphology, structure and optical properties were characterized by TEM, SED, UV-vis spectra and PL spectra. The results show that the products are hexagonal ZnS nanocrystals with 15 nm-215 nm in diameter. The morphology and dimension of ZnS nanoparticles could be controlled by varying the sulfaration time. The UV-vis absorption spectra indicate that the absorption edges are blue-shifted by shortening the sulfuration time, exhibiting a marked quantum size effect. With shortening sulfuration time, the photoluminescence emission peak of 409.8 nm is blue-shifted, which could be ascribed to be the forbidden gap emission.
Synthesis of lead sulfide nanocrystals via microwave and sonochemical methods

Yu Zhao,Xue-Hong Liao,Jian-Min Hong,Jun-Jie Zhu

DOI: https://doi.org/10.1016/j.matchemphys.2004.05.026

IF: 4.778

2004-01-01

Materials Chemistry and Physics

Abstract:Lead sulfide nanocrystals have been prepared by two novel routes in microwave heating and ultrasonic irradiation. In the experiments, lead acetate and thiourea are used as lead source and sulfur source, respectively. Different size and morphology of lead sulfide (PbS) nanocrystals can be obtained by using ethanol, distilled water, ethylene glycol and polyethylene glycol-200 as solvents. X-ray diffraction results show that the as-prepared PbS nanocrystals have a cubic structure. Probable mechanisms for the formation of PbS particles are also proposed.
Microwave-Assisted Aqueous Synthesis: A Rapid Approach to Prepare Highly Luminescent Znse(S) Alloyed Quantum Dots

HF Qian,X Qiu,L Li,JC Ren

DOI: https://doi.org/10.1021/jp0539324

2006-01-01

Abstract:In this paper, we present a new procedure for the rapid synthesis of luminescent ZnSe nanocrystals in aqueous phase by microwave irradiation with controllable temperature. The effects of microwave irradiation and experimental conditions on the synthesis of nanocrystals were investigated systematically. It was found that there were significant effects of pH value of reaction solutions, molar ratio of precursors, and heating time of microwave irradiation on the optical properties of the ZnSe nanocrystals. A series of nanocrystals with different size was prepared in 1 h, and the photoluminescence quantum yield reached up to 17% at the optimal reaction condition. The results of HRTEM and XRD showed that the as-prepared nanocrystals had high crystallinity. The characterizations of EDS spectra and elemental analysis showed that the sulfur content of nanocrystals increased with the growth of nanocrystals. We speculated that the structure of nanocrystals was an alloy ZnSe(S) shell on the surface of the ZnSe particles core. Furthermore, we found that the oxygen from air in the reaction vessel played an important role in the decomposition of the thiol group under microwave irradiation.
A microwave assisted heating method for the preparation of copper sulfide nanorods

Xue-Hong Liao,Nian-You Chen,Shu Xu,Shui-Bin Yang,Jun-Jie Zhu

DOI: https://doi.org/10.1016/S0022-0248(03)01030-3

IF: 1.8

2003-01-01

Journal of Crystal Growth

Abstract:Copper sulfide nanorods have been prepared by microwave irradiation of 1% (w/v) sodium dodecyl sulfate aqueous solution of copper nitrate and thioacetamide. Powder X-ray diffraction pattern indicated that the product was pure hexagonal phase copper sulfide. The product was also characterized by the techniques of transmission electron microscopy and X-ray photoelectron diffraction.
Synthesis of CuO Nanoparticles by Microwave Irradiation

Yang Han-min

Abstract:Using Cu(Ac)2 as precursor,CuO nanoparticles were prepared under microwave irradiation.The CuO nanoparticles were studied by using TEM,XRD analyzer.The results showed that CuO nanoparticles with good dispersibility were synthesized via the novel method mentioned above.Microwave(MW) heating was a rapid and effective way to prepare CuO nanoparticles.The morphology of CuO nanoparticles varied with different solvent and complex.PVP(Polyvinylpyrrolidone) was benefit to the dispersing and stablizion of CuO nanoparticles in solvent.

Chemistry,Materials Science
Microwave assisted preparation of CdSe, PbSe, and Cu2-xSe nanoparticles

Junjie Zhu,Oleg Palchik,Siguang Chen,Aharon Gedanken

2000-01-01

Abstract:Nanoparticles of various dimensions of II-VI binary chalcogenides CdSe, PbSe, and Cu2-xSe, have been prepared by a very simple fast reaction between acetates or sulfates of Cd, Pb, and Cu and Na2SeSO3 in the presence of complexating agents, using microwave irradiation. The nanoparticles were analyzed by X-ray diffraction (XRD), electron" microscopy (TEM) and X-ray photoelectron spectroscopy (XPS). © 2000 American Chemical Society.
Rapid Fabrication and Optical Properties of Zinc Sulfide Nanocrystallines in a Heterogeneous System

YH Ni,G Yin,JM Hong,Z Xu

DOI: https://doi.org/10.1016/j.materresbull.2004.01.011

IF: 5.6

2004-01-01

Materials Research Bulletin

Abstract:ZnS nanoparticles about 3nm in size were prepared by a simple, rapid and reliable route under microwave irradiation in a heterogeneous system, using ZnAc2·2H2O (AcCH3COO) and Na2S·9H2O as the starting materials, ethylene glycol (EG) as the medium. The product was characterized with X-ray powder diffraction (XRD), transmission electron microscopy (TEM) and ED, respectively. The optical properties of ZnS nanoparticles were studied.
Preparation and Properties of Nanoparticles ZnS

ZHOU Xiang-ling,ZHENG Yu-feng,LI Qian,GUO Fu-qiang,SUN Yi-fei

DOI: https://doi.org/10.16818/j.issn1001-5868.2008.02.017

2008-01-01

Abstract:Nanoparticles of spheres-like zinc sulphide were synthesized via the hydrothermal route.The effects of preparation parameters such as mol,reaction temperature,growth time condition on ZnS particles' morpho-logy and size were discussed.The particles were characterized by X-ray diffraction(XRD),and transmission electron microscopy(TEM),and then UV-VIS was used to study the sample's optical properties.
Preparation of CuO Nanoparticles by Microwave Irradiation

H Wang,JZ Xu,JJ Zhu,HY Chen

DOI: https://doi.org/10.1016/s0022-0248(02)01571-3

IF: 1.8

2002-01-01

Journal of Crystal Growth

Abstract:CuO nanoparticles with an average size of ca. 4nm have been successfully prepared by microwave irradiation, using copper (II) acetate and sodium hydroxide as the starting materials and ethanol as the solvent. The CuO nanoparticles are characterized by using techniques such as X-ray powder diffraction, transmission electron microscopy, selected area electron diffraction, X-ray photoelectron spectroscopy and UV–Visible absorption spectroscopy. The as-prepared CuO nanoparticles have regular shape, narrow size distribution and high purity. The band gap is estimated to be 2.43eV according to the results of the optical measurements of the CuO nanoparticles.
Microwave-assisted self-assembled ZnS nanoballs

Yu Zhao,J.-M. Hong,J.-J. Zhu

DOI: https://doi.org/10.1016/j.jcrysgro.2004.06.036

IF: 1.8

2004-01-01

Journal of Crystal Growth

Abstract:Self-assembled zinc sulfide nanoballs were prepared in saturated aqueous solutions via a microwave-assisted route. Zinc acetate and thioacetamide were selected as zinc source and sulfur source, respectively. Powder X-ray diffraction, transmission electron microscopy, selected area electron diffraction, X-ray photoelectron spectra, Fourier transform infrared and Thermogravimetric analysis were used to characterize the as-prepared products and the optical properties was studied by diffuse reflection spectra and photoluminescence spectra. Zinc sulfate and zinc nitrite can also used to prepare ZnS nanoparticles instead of nanoballs. The mechanism for the assembly of ZnS nanoballs was also discussed.
Preparation and characterization of ZnS nanostructures

Caifeng Wang,Bo Hu,Ligang Chen,Ni Liu,Jie Li

DOI: https://doi.org/10.1016/j.ijleo.2020.165673

IF: 3.1

2020-12-01

Optik

Abstract:ZnS nanostructures were prepared using different S sources precursor solution by hydrothermal method, and the crystalline structure, surface morphologies and optical properties were studied in detail. XRD patterns show that all samples have a diffraction peak near 28.5°, corresponding to crystal direction (111) of β-ZnS. SEM diagrams show that ZnS nanostructures prepared using TAA and thiourea are spherical and granular, while ZnS prepared using Na2S is irregular and grainy, with some larger blocky structures. EDS spectra show that the chemical element ratio (Zn:S) of ZnS prepared using thiourea is closest to 1:1. The PL peaks of ZnS prepared using TAA and Na2S are around 450 nm, while that of ZnS prepared using thiourea has a green light emission centered at 530 nm with a shoulder peak at 570 nm, and the emission intensity is very strong. Therefore, ZnS nanostructures prepared using thiourea as S source are more suitable for optical devices.

optics
Preparation of Bi2S3 nanorods by microwave irradiation

Xue-Hong Liao,Hui Wang,Jun-Jie Zhu,Hong-Yuan Chen

DOI: https://doi.org/10.1016/S0025-5408(01)00734-6

IF: 5.6

2001-01-01

Materials Research Bulletin

Abstract:Bi2S3 nanorods, with a diameter of ca. 10 nm and a length of up to ca. 300 nm, have been successfully prepared from a formaldehyde solution of bismuth nitrate and thiourea by microwave irradiation. Powder X-ray diffraction (XRD) pattern indicates that the product is pure orthorhombic Bi2S3 phase. The product is also characterized by the techniques of transmission electron microscopy (TEM) and X-ray photoelectron spectra (XPS).
Preparation and characterization of ZnS/poly(acrylamide-co-acrylic acid) dendritical nanocomposites by γ-irradiation

Yong-hong Ni,Xue-wu Ge,Zhi-cheng Zhang

DOI: https://doi.org/10.1016/j.mseb.2005.01.003

2005-01-01

Abstract:Zinc sulfide poly(acrylamide-co-acrylic acid) [ZnS/P(AM-co-AA)] nanocomposites with a dendritical structure were successfully prepared in one step by γ-irradiation technique in an aqueous system at room temperature and under ambient pressure. The results from X-ray powder diffraction (XRD) analysis and IR spectrum of the final product showed the formation of ZnS nanoparticles and the polymerization of monomers, respectively. The photoluminescence (PL) peak of the as-prepared product centered at 450nm, which showed an obvious red shift compared with the ZnS bulk material. The presence of copolymer was considered to be the main reason that influenced the shape and photoluminescence property of the composite.
Sno2 and Zno Nanostructured Spheres Self-Assembled by Nanocrystals: Microwave-Assisted Preparation and Enhancement of Photocatalytic Activity

Ling Zhang,Ying-Jie Zhu,Shao-Wen Cao

DOI: https://doi.org/10.1246/cl.2008.1002

2008-01-01

Chemistry Letters

Abstract:We have developed a simple microwave-assisted solvothermal method for the preparation of SnO2 and ZnO hierarchically nanostructured spheres self-assembled by nanocrystals. The photocatalytic activity is significantly enhanced by simply mixing SnO2 and ZnO nanostructured spheres without any treatment or processing.

Preparation of Semiconductor ZnS Nanoparticles with Microwave Irradiation

Preparation of CdS and ZnS nanoparticles using microwave irradiation

Preparation of Zns Nanoparticles by Ultrasonic Radiation Method

Formation of Monodispersed Pvp-Capped Zns and Cds Nanocrystals under Microwave Irradiation

γ-Irradiation preparation and characterization of nanocrystalline ZnS

Microwave Synthesis Of Nanocrystalline Metal Sulfides In Formaldehyde Solution

Microwave Assisted Preparation of CdSe , PbSe , and Cu 2x Se Nanoparticles

Studies of synthesis and optical properties of ZnS nanocrystals

Synthesis of lead sulfide nanocrystals via microwave and sonochemical methods

Microwave-Assisted Aqueous Synthesis: A Rapid Approach to Prepare Highly Luminescent Znse(S) Alloyed Quantum Dots

A microwave assisted heating method for the preparation of copper sulfide nanorods

Synthesis of CuO Nanoparticles by Microwave Irradiation

Microwave assisted preparation of CdSe, PbSe, and Cu2-xSe nanoparticles

Rapid Fabrication and Optical Properties of Zinc Sulfide Nanocrystallines in a Heterogeneous System

Preparation and Properties of Nanoparticles ZnS

Preparation of CuO Nanoparticles by Microwave Irradiation

Microwave-assisted self-assembled ZnS nanoballs

Preparation and characterization of ZnS nanostructures

Preparation of Bi2S3 nanorods by microwave irradiation

Preparation and characterization of ZnS/poly(acrylamide-co-acrylic acid) dendritical nanocomposites by γ-irradiation

Sno2 and Zno Nanostructured Spheres Self-Assembled by Nanocrystals: Microwave-Assisted Preparation and Enhancement of Photocatalytic Activity