Abstract:Chitosan (CS) is one promising material as a temporary mechanical supporter for bone fracture internal fixation. In our previous work, we successfully fabricated CS rods through one in situ precipitation route. But bending strength and bending modulus of CS rods need to be improved to match the commercially available devices used for bone fracture internal fixation. In this research, CS rods were reinforced effectively through cross-linking reaction by using glutaraldehyde as the coupling reagent. Schiff’s base was detected by FTIR due to the chemical reaction between amino groups and aldehyde groups. Crystal plane space of CS rods became small during the formation of network structure. Microstructure was observed by SEM, indicating that layer-by-layer structure became much tighter after cross-linking reaction, and cracks in one layer turned around when they reached another layer to absorb energy. Bending strength and bending modulus of cross-linked CS rods could reach 186.3 MPa and 5.17 GPa, respectively. Compared with uncross-linked CS rods, they are increased by 101.6% and 26.1%, respectively. As a result, mechanical properties of CS rods are equivalent to the commercially available biodegradable devices. CS rods with excellent mechanical properties are a good candidate for bone fracture internal fixation.

Chitosan Rods with Annual Ring Structure Prepared Via Grade-Pervasion Precipitation

Preparation and Characterization of Three Dimensions Chitosan Rods with Biomimetic Layered Structure Similar to Annual Ring

Preparation of Chitosan Rods with Excellent Mechanical Properties: One Candidate for Bone Fracture Internal Fixation

Chitosan Rod Reinforced with Absorbent Cotton Fibers

Chitosan Rods Reinforced by N-Carboxyl Propionyl Chitosan Sodium

Chitosan and Multi-Walled Carbon Nanotube Composite Rods

Chitosan rod reinforced by self-crosslinking through thermal treatment

Chitin Fiber and Chitosan 3D Composite Rods

High strength chitosan rod reinforced by non-covalent functionalized multiwalled carbon nanotubes via an in situ precipitation method

Preparation and properties of three-dimensional hydroxyapatite/chitosan nanocomposite rods.

High Strength Chitosan Rod Prepared Via LiOH/urea Solvent Through Centrifugation Induced Orientation Processing

Chitosan Rods Reinforced by Aligned Multiwalled Carbon Nanotubes Via Magnetic-Field-Assistant in Situ Precipitation

Preparation and Characterization of Cellulose Fiber/chitosan Composites

Biomineralization Behavior of Biomimetic Chitosan Rod

Biomimetic Multi-Layered Hollow Chitosan–tripolyphosphate Rod with Excellent Mechanical Performance

Synthesis and Characterization of Chitosan Oligosaccharide-graft-Acrylic Acid Biodegradable Crosslinker

Layered Chitosan Conduits with Controllable Inner Diameters

A facile approach to construct three-dimensional oriented chitosan scaffolds with in-situ precipitation method

Study of the Mechanical Property of Magnetite/ Hydroxyapatite/ Chitosan Nano-Composite

Preparation and Structure of Chitosan Swellable in Alkali Solution by Ultrasonic Treatment

Preparation of Chitosan/Hydroxyapatite Nanocomposite with Layered Structure Via In-Situ Compositing