HIGH TEMPERATURE SOLUTION GROWTH AND STRUCTURE CHARACTERIZATION OF FERROELECTROMAGNET Pb(Fe_(1/2)Nb_(1/2))O_3 SINGLE CRYSTALS

Yingkui Yang,Liu Jun-Ming

2005-01-01

Abstract:Single crystals of Pb(Fe_(1/2)Nb_(1/2))O_3 (PFN) in size of 3 mm×3 mm×3 mm were grown by high temperature solution method with slow cooling from a molten flux of PbO and applied the temperature oscillation during nuclei. The X-ray diffraction from 80 K to 400 K and Raman spectra with temperature change from 80 K to 450 K were used to characterize the obtained crystal structure symmetry. The results show that PFN is in rhombohedron structure from 80 K to its ferroelectric phase transformation temperature at 383 K. Over antiferromagnetic phase transition temperature, the diagonal of PFN crystal cell gradually gets short, and below Neel critical point the structure of PFN crystal no change. The peaks of Raman spectra no change at temperature of 80—200 K, indicating that there is no change in structure within this temperature range. The experimental results are useful for the further investigation on the mechanism of ferroelectromagnets.