Enhanced High-Temperature Energy Storage Properties in BNT-based Ceramics with Well-Controlled Low Dielectric Loss

Xinheng Li,Hang Yang,Chaoqiong Zhu,Shiheng Li,Aoyu Li,Ziming Cai,Peizhong Feng

DOI: https://doi.org/10.1016/j.ceramint.2023.10.233

IF: 5.532

2023-01-01

Ceramics International

Abstract:High-temperature resistance is one of the hot topics in the development of high-power density dielectric materials. It is still a great challenge for dielectric materials to meet the requirements of high energy density and low energy loss at high temperature. Based on the philosophy of increasing the Curie temperature and decreasing the dielectric loss at high temperature, a ceramic system of (1-x)Bi0.5Na0.5TiO3-xBi(Mg0.3Zr0.6)O-3 ((1-x)BNT-xBMZ) is designed to improve the high-temperature energy storage properties. The Curie temperature was significantly increased from 320 degrees C to nearly 400 degrees C, and the dielectric loss was controlled below 5% up to 400 degrees C in the 0.92BNT-0.08BMZ ceramic. Due to the high Curie temperature and low dielectric loss, the maximum polarization and discharge energy density at 200 degrees C under 200 kV/cm of the 0.92BNT-0.08BMZ ceramic sample are as high as 48.79 mu C/cm(2) and 3.73 J/cm(3), respectively. With the BMZ content increases, the changing rate of Pmax in the temperature range of 30 similar to 200 degrees C decreases from 18.76% for the x = 0.06 ceramic to 10.27% for the x = 0.10 ceramic under 120 kV/cm, and the remanent polarization decreases from 5.23 mu C/cm(2) to 2.55 mu C/cm(2) at 200 degrees C, correspondingly. All these characteristics show that (1-x)BNT-xBMZ ceramics have broad application prospects in the field of high-temperature energy storage systems.