Polyoxometalate@ZIF Induced CoWO 4 /WS 2 @C-N Nanoflower as a Highly Efficient Catalyst for Zn–Air Batteries
Di Yin,Ming-Liang Wang,Yun-Dong Cao,Xiaopeng Yang,Su-Yu Ji,Hui-Ping Hao,Guang-Gang Gao,Lin-Lin Fan,Hong Liu
DOI: https://doi.org/10.1021/acsaem.1c01000
IF: 6.4
2021-07-08
ACS Applied Energy Materials
Abstract:It is crucial to cultivate competent and stable bifunctional electrocatalysts for both the oxygen reduction reaction (ORR) and the oxygen evolution reaction (OER). In this work, a high-performance and long-lasting electrocatalyst of CoWO<sub>4</sub>/WS<sub>2</sub>@C-N nanocomposite with the unique hierarchical flowerlike superstructure is achieved by sulfuration of porous precursor, in which the polyoxometalate acts as both template and acidic etching agent. The introduction of polyoxometalate also plays a key role in forming the binary CoWO<sub>4</sub>/WS<sub>2</sub> active center during the sulfuration process. CoWO<sub>4</sub>/WS<sub>2</sub>@C-N electrocatalyst shows higher electrocatalytic activity than commercial noble-metal catalysts under the same conditions. DFT calculations indicate that both the high adsorption energy for the OH<sup>–</sup> group and low adsorption energy for O<sub>2</sub> on the surface of CoWO<sub>4</sub>/WS<sub>2</sub> sites result in high OER and ORR activity. When CoWO<sub>4</sub>/WS<sub>2</sub>@C-N is assembled in a lab-made Zn–air battery as cathode material, the battery shows a higher discharge plateau voltage of 1.46 V and a specific capacity of 664 mA h g<sub>Zn</sub><sup>–1</sup>, the behavior of which is comparable to the reported non-noble-metal materials. The synthetic strategy presented in this work not only opens a polyoxometalate-etching-ZIF way to constructing a nanosized heterojunction catalyst but also provides a cost-effective and robust electrocatalyst potentially used in practical Zn–air batteries.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsaem.1c01000?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsaem.1c01000</a>.Materials, characterizations, electrochemical measurements, and calculation details; FTIR, P-XRD, TG of PW<sub>12</sub>, ZIF-67, and PW<sub>12</sub>@ZIF-67; P-XRD, EDS, K–L plots, and stability test of CoWO<sub>4</sub>/WS<sub>2</sub>@C-N; P-XRD and OER polarization curves of CoWO<sub>4</sub>/WS<sub>2</sub>@C-N at different pyrolysis temperatures; TEM and XPS of CoWO<sub>4</sub>/WS<sub>2</sub>@C-N after long-term discharge and charge processes; and comparison of ORR, OER, and Zn–air batteries performance for other reported cobalt-based catalysts (<a class="ext-link" href="/doi/suppl/10.1021/acsaem.1c01000/suppl_file/ae1c01000_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.
materials science, multidisciplinary,chemistry, physical,energy & fuels