Abstract:An efficient reduction method to obtain high-quality graphene sheets from mass-producible graphene oxide is highly desirable for practical applications. Here, we report an in situ deoxidation and graphitization mechanism for graphene oxide that allows for high-quality reduced graphene oxide sheets under the low temperature condition (<300 °C) by utilizing a well-known Fischer–Tropsch reaction catalyst (CuFeO2). By applying modified FTR conditions, where graphene oxide was reduced on the catalyst surface under the hydrogen-poor condition, deoxidation with much suppressed carbon loss was possible, resulting in high-quality graphene sheets. Our experimental data and density functional theory calculations proved that reduction which occurred on the CuFeO2 surface preferentially removed adsorbed oxygen atoms in graphene oxide sheets, leaving dissociated carbon structures to be restored to a near-perfect few-layer graphene sheet. TGA-mass data revealed that GO with catalysts released 92.8% less carbon-containing gases than GO without catalysts during the reduction process, which suggests that this process suppressed carbon loss in graphene oxide sheets, leading to near-perfect graphene. The amount of oxygen related to the epoxide group in the basal plane of GO significantly decreased to near zero (from 43.84 to 0.48 at. %) in catalyst-assisted reduced graphene oxide (CA-rGO). The average domain size and the density of defects of CA-rGO were 4 times larger and 0.1 times lower than those for thermally reduced graphene oxide (TrGO), respectively. As a result, CA-rGO had a 246 and 8 times lower electrical resistance than TrGO and CVD-graphene. With these performances, CA-rGO coated paper connected to a coin-cell battery successfully lit an LED bulb, and CA-rGO itself acted as an efficient catalyst for both the hydrogen evolution reaction and the oxygen evolution reaction.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsnano.1c02178?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsnano.1c02178</a>.SEM, TEM, and AFM images of catalysts and GO; additional data of CA-rGO (Raman, optical image, XRD, and electrical data); ID/IG ratio, XPS, UV–vis spectra, FT-IR spectra of samples prepared with different conditions; GC-mass analysis, TOF-SIMS, and ICP data for the reduction mechanism (<a class="ext-link" href="/doi/suppl/10.1021/acsnano.1c02178/suppl_file/nn1c02178_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.

Rapid Microwave Reduction of Electrochemically-Derived Graphene Oxide for High-Crystalline Graphene Membranes

Selective Reduction of Epoxy Groups in Graphene Oxide Membrane for Ultrahigh Water Permeation

A New Reducing Agent to Prepare Single-Layer, High-Quality Reduced Graphene Oxide for Device Applications

Rapid Effective Reduction by Microwave-Irradiated Thermal Reaction for Large-Scale Production of High-Quality Reduced Graphene Oxide

Back Cover: A Catalytic Microwave Process for Superfast Preparation of High‐Quality Reduced Graphene Oxide (angew. Chem. Int. Ed. 49/2017)

Preparation of Reduced Graphene Oxide by Infrared Irradiation Induced Photothermal Reduction

Electrochemical Synthesis of Graphene Oxide from Graphite Flakes Exfoliated at Room Temperature

Modulation of Interlayer Nanochannels via the Moderate Heat Treatment of Graphene Oxide Membranes

Enhancing the Dye-Rejection Efficiencies and Stability of Graphene Oxide-Based Nanofiltration Membranes via Divalent Cation Intercalation and Mild Reduction

Highly Efficient Preparation of Graphite Oxide without Water Enhanced Oxidation

Hydrothermal Reduced Graphene Oxide Membranes for Dyes Removing

Effect of Microwave Treatment in a High Pressure Microwave Reactor on Graphene Oxide Reduction Process-TEM, XRD, Raman, IR and Surface Electron Spectroscopic Studies

New Structural Insights into Densely Assembled Reduced Graphene Oxide Membranes

Photoreduction of Graphene Oxides: Methods, Properties, and Applications

In-situ reduction of graphene oxide for electrochemical supercapacitor application

Engineering Reduced Graphene Oxides with Enhanced Electrochemical Properties Through Multiple-Step Reductions

Surface Charge and Hydrophilicity Improvement of Graphene Membranes Via Modification of Pore Surface Oxygen-Containing Groups to Enhance Permeability and Selectivity

Graphitization with Suppressed Carbon Loss for High-Quality Reduced Graphene Oxide

Highly efficient restoration of graphitic structure in graphene oxide using alcohol vapors.

Graphene Oxide Prompted Double-Crosslinked Poly(Vinyl Alcohol)/Poly(Diallyldimethylammonium Chloride) Anion-Exchange Membrane for Superior Co2 Electrochemical Reduction

A Non-Heat-Source Process for Preparing Graphene Oxide with Low Energy Consumption