Effect of CeO<inf>2</inf> particles on the high phosphorus electroless Ni layer

Zhen Zheng,An Rong,Zhou Wei,Zhou Shuya,Chunqing Wang

DOI: https://doi.org/10.1109/ICEPT.2015.7236630

2015-01-01

Abstract:Electroless Ni (EN) technology is widely used in electronic package field and the high phosphorus composite EN technology was studied. In this paper, we discussed the influence of nano-CeO <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</sub> and micro-CeO <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</sub> particles with different amounts when they were added in high phosphorus content Ni-P composite coating. The microstructure and crystal structure of the coating were observed by scanning electron microscope (SEM) and X-ray diffraction analysis (XRD) respectively. The results showed that whether nano-CeO <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</sub> or micro-CeO <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</sub> , both refined the grain, increased the specific surface area, however the micro-CeO <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</sub> particles made more obvious effect. As the XRD result showed, the peak gradually become gentle, the coating turned into amorphous which may cause by the CeO <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</sub> particles absorbed in the grain boundary and crystal defects. The results indicated the CeO <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</sub> deposited with the coating very well. Finally, the corrosion resistance of the coating was tested with the method of electrochemical impedance (EIS) and linear polarization. The results were unified. When the dosage is 5g/L, the corrosion resistance was the best. However, lower corrosion resistance was got when excessive CeO <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</sub> particles were added which may affect by the catalytic property.