Enhancement Actuation Mechanism for the Sheath-Run Artificial Muscle Fiber under Weak Current

Zenghui Zhao,Sufeng Zhu,Guang Yang,Xufeng Dong,Jiangtao Di,Min Qi,Hao Huang

DOI: https://doi.org/10.1007/s40843-023-2618-5

2023-01-01

Science China Materials

Abstract:Electrothermal sheath-run artificial muscles hold great promise for various applications. Their sheath expands and softens when subjected to Joule heat generated by high currents, effectively releasing the stored torsional energy within the core fiber. This phenomenon significantly enhances actuation performance. In this study, an artificial muscle composed of pre-twisted carbon nanotube (CNT) fiber encased in polydimethylsiloxane (PDMS) sheath was prepared. Under a 50-mA current at a frequency of 0.25 Hz, it demonstrated a 13.28% contraction stroke and 9.82 MPa contraction stress, with a power density of 3.8 W g −1 . Notably, thanks to its non-coiled structure, CNT fiber@PDMS can operate at speeds of up to 42% s −1 , and be applied to switches and biomimetic arms. Interestingly, we observed improved actuation performance even with relatively weak currents that were insufficient to induce the expansion and softening of the PDMS sheath typically required for actuation. To explain this phenomenon, a mechanism involving the densification of the CNT fiber by the PDMS sheath was proposed. When electrified, the CNT fiber initiates Ampere attraction forces among its internal CNTs, generating actuation. Simultaneously, the curing process of the PDMS sheath induces radial compressive stresses, reducing the spacing between CNTs and thereby increasing the Ampere attraction force. We substantiated this mechanism through investigations into actuation behavior at different temperatures, internal microstructure, and the mechanical and electrical properties of the CNT fiber@PDMS, ultimately providing a comprehensive analysis of energy changes throughout the actuation process.