Abstract:The initiation and early-stage crack growth under very-high-cycle fatigue (VHCF) at room temperature, 750 °C, and 850 °C on directionally solidified Ni-base superalloy have been investigated. There was little frequency effect of 20 kHz on fatigue lives when compared with 100 Hz, nor did the deformation and fracture mechanisms. Dislocation tangles re-arranged themselves to form well-defined networks at interface of γ / γ ′, accounting for the enhanced fatigue strength at 850 °C in VHCF regime when compared to that at 750 °C. In most cases, internal casting pore was the crack initiation site. Crack initiation and early-stage growth occurred on one of the {111} planes or their intersecting planes, a characteristic of Stage I cracking. With the use of optimized intermittent loading conditions, both the initiation and early-stage crack growth processes were successfully tracked on the basis of fine but visible beach marks within the Stage I cracking region. The first registered fatigue beach mark can be as close as only 86 μ m to the crack initiation site and the crack length increased steadily over the whole early-stage crack growth stage. The enhanced fatigue strength at 850 °C can be rationalized with the higher threshold for propagating the early-stage crack. The fraction of fatigue life consumed for early-stage crack growth reduces with the decreasing stress, eventually leading to the initiation-controlling VHCF fatigue failure. The implications of these results are discussed with respect to the model prediction of fatigue life and fatigue strength.

Crack Initiation in Ni-Based Single Crystal Superalloy under Low-Cycle Fatigue-Oxidation Conditions

Transition from Internal to Surface Crack Initiation of a Single-Crystal Superalloy in the Very-High-cycle Fatigue Regime at 1100 °C

Computational Modelling of Crack Initiation in a Single Crystal Superalloy under Fatigue–oxidation Conditions

Microscopic Damage and Fracture Mechanism of Nickel-based Single Crystal Superalloy during Low Cycle Fatigue at Elevated Temperature

Low Cycle Fatigue Failure Analysis of a Ni‐Based Single Crystal Superalloys at 850 °C

High-cycle Fatigue Behaviour and Crack Growth Mechanism of Ni-base Single Crystal Superalloy under Intermediate Temperature

Crack Initiation Behavior of a Ni-based SX Superalloy under Transient Thermal Stress

Influence of Strain Amplitude on Low-Cycle Fatigue Behaviors of a Fourth-Generation Ni-Based Single-Crystal Superalloy at 980 °C

In-situ Observation of Crack Initiation and Propagation in Ni-based Superalloy with Film Cooling Holes During Tensile Test

Oxidation Behavior and Mechanism of a Ni-based Single Crystal Superalloy with Single Α-Al2o3 Film at 1000 °C

Low Cycle Fatigue Behavior and Crack Initiation Mechanism of Ni-based Single Crystal Curved Thin-Walled Blade Simulator Specimen with Film Cooling Holes

Transient Thermal Fatigue Crack Propagation Behavior of a Nickel-Based Single-Crystal Superalloy

4731 - PREDICTION OF CRACK INITIATION IN SINGLE CRYSTAL Ni-BASE SUPERALLOYS AT HIGH TEMPERATURES

Oxidation-induced recrystallization and damage mechanism of a Ni-based single-crystal superalloy during creep

Influence of Surface Roughness on the Oxidation Behavior of a Ni-4.0Cr-5.7Al Single Crystal Superalloy

Mechanism of Low Cycle Fatigue Damage for Nickel-Based Powder Superalloy

Investigation on Microstructure Evolution and Fracture Morphology of Single Crystal Nickel-Base Superalloys under Creep-Fatigue Interaction Loading

Oxygen Changes Crack Modes of Ni-based Single Crystal Superalloy

Crack Initiation and Propagation Behaviour under High-Temperature Very-High-cycle Fatigue: Directionally Solidified Columnar-Grained Vs. Single-Crystal Superalloys

Low-cycle Fatigue Behavior of Coated and Uncoated Single Crystal Ni-based Superalloy at Various Temperatures

Initiation and Early-Stage Growth of Internal Fatigue Cracking under Very-High-Cycle Fatigue Regime at High Temperature