Stimulating the C−C coupling ability of ultrafine copper nanoclusters via nitrogen coordination for electrocatalytic CO 2 reduction
Yanan Cao,Guodong Sun,Mingzhen Hu,Zhe Wang,Xiaoxin Yang,Xinhu Liang,Zengjian Cai,Hao Ren,Fengyi Shen,Dan Cheng,Kebin Zhou
DOI: https://doi.org/10.1016/j.apcatb.2024.124704
IF: 24.319
2024-10-17
Applied Catalysis B Environmental
Abstract:Cu-based materials are widely regarded as the most effective electrocatalysts for selectively reducing CO 2 to multi-carbon products. Nevertheless, the ultrafine Cu nanoclusters are generally inefficient in electro-reducing CO 2 to multi-carbon products because of their exceptionally high d-band center, which leads to binding with the CO intermediates strongly and impeding the C−C coupling. Herein, we report that a nitrogen coordination strategy can significantly stimulate the ultrafine copper nanoclusters' C−C coupling ability. Strikingly, the Faradaic efficiency (FE) of CO 2 -to-C 2 H 4 over the N-coordinated Cu nanoclusters on nitrogen-modified carbon support (Cu-N/NC) is up to 61.4 % with a current density of −208 mA cm −2 at −1.05 V (vs RHE), which is much superior to the pure copper nanoclusters/nanoparticles (FE(C 2 H 4 )<5 %). Theoretical calculations unveil that the N coordination can optimize the d-band center of copper clusters and its adsorption energy toward *CO, which largely reduces the energy barrier of the C−C coupling step (from 1.28 eV to 0.35 eV) and thus improves the C 2 H 4 selectivity. In-situ Raman spectra and CO-TPD tests prove that the Cu-N/NC catalyst exhibits the best CO adsorption strength to benefit C−C coupling. Moreover, the CO 2 reduction current density of the Cu-N/NC catalyst remains stable at about 210 mA cm −2 with the FE(C 2 H 4 ) remaining at about 60 % during a 12-hour durability test, showing excellent catalytic stability.
chemistry, physical,engineering, chemical, environmental