Abstract:This paper describes a solution-phase synthesis of high-quality vanadium dioxide thermochromic thin films. The films obtained showed excellent visible transparency and a large change in transmittance at near-infrared (NIR) wavelengths before and after the metal-insulator phase transition (MIPT). For a 59 nm thick single-layer VO(2) thin film, the integral values of visible transmittance (T(int)) for metallic (M) and semiconductive (S) states were 54.1% and 49.1%, respectively, while the NIR switching efficiencies (DeltaT) were as high as 50% at 2000 nm. Thinner films can provide much higher transmittance of visible light, but they suffer from an attenuation of the switching efficiency in the near-infrared region. By varying the film thickness, ultrahigh T(int) values of 75.2% and 75.7% for the M and S states, respectively, were obtained, while the DeltaT at 2000 nm remained high. These results represent the best data for VO(2) to date. Thicker films in an optimized range can give enhanced NIR switching efficiencies and excellent NIR blocking abilities; in a particularly impressive experiment, one film provided near-zero NIR transmittance in the switched state. The thickness-dependent performance suggests that VO(2) will be of great use in the objective-specific applications. The reflectance and emissivity at the wavelength range of 2.5-25 microm before and after the MIPT were dependent on the film thickness; large contrasts were observed for relatively thick films. This work also showed that the MIPT temperature can be reduced simply by selecting the annealing temperature that induces local nonstoichiometry; a MIPT temperature as low as 42.7 degrees C was obtained by annealing the film at 440 degrees C. These properties (the high visible transmittance, the large change in infrared transmittance, and the near room-temperature MIPT) suggest that the current method is a landmark in the development of this interesting material toward applications in energy-saving smart windows.

Fully Discrete VO2 Particulate Film with Ultra‐High Transmittance and Excellent Thermochromic Performance

Fully Discrete VO 2 Particulate Film with Ultra‐High Transmittance and Excellent Thermochromic Performance

Enhancing Thermochromic Performance of VO2 Films Via Increased Microroughness by Phase Separation

Solution-Based Fabrication of Vanadium Dioxide on F:Sno2 Substrates with Largely Enhanced Thermochromism and Low-Emissivity for Energy-Saving Applications

Thermochromic VO2 thin films: solution-based processing, improved optical properties, and lowered phase transformation temperature

Facile Preparation of Double-Sided Vo2 (M) Films with Micro-Structure and Enhanced Thermochromic Performances

Enhanced visible and tunable infrared transmittance of W-doped VO2/SiO2/PVP composite films for smart windows

High thermochromic performance of Fe/Mg co-doped VO2 thin films for smart window applications

3D Ordered Macroporous VO2 Thin Films with an Efficient Thermochromic Modulation Capability for Advanced Smart Windows

VO2-ZnO Composite Films with Enhanced Thermochromic Properties for Smart Windows

Solution-Processed VO 2 -SiO 2 Composite Films with Simultaneously Enhanced Luminous Transmittance, Solar Modulation Ability and Anti-Oxidation property

Enhanced Thermochromic Performance of VO<sub>2</sub> Nanoparticles by Quenching Process

Enhanced Thermochromic Performance of VO2 Nanoparticles by Quenching Process

Solution-processed VO2-SiO2 composite films with simultaneously enhanced luminous transmittance, solar modulation ability and anti-oxidation property

Sputtering Flexible VO2 Films for Effective Thermal Modulation.

Vanadium Dioxide for Thermochromic Smart Windows in Ambient Conditions

Self-templated method to fabricate VO2 nanoparticles with ultrahigh luminous transmittance for energy-efficient thermochromic windows

Double-layer VO2 Thin Film Patterned by SiO2 Spheres with Improved Thermochromic Properties for Smart Windows

A low cost preparation of VO2 thin films with improved thermochromic properties from a solution-based process

Novel warm/cool-tone switchable VO2-based smart window composite films with excellent optical performance

Enhanced Visible Transmittance with Low Phase Transition Temperature of Vo2 Enabled by W-Mg Co-Doping