Abstract:Inspired by the excellent activity of platinum in hydrogen evolution reaction (HER) and the good performance of Ni-based compounds in oxygen evolution reaction (OER), a bifunctional electrocatalyst PtNi carbon nanofiber (CNF) is designed and fabricated using electrospinning followed by carbonization. Ultra-small PtNi nanoparticles of several nanometers in size are densely dispersed on every CNF, along with a few larger nanoparticles with sizes of several decades of nanometers. The as-prepared catalysts can be directly used as an electrode and act as high-efficiency materials for water splitting, including HER and OER. For HER activity, the PtNi/CNFs reach 10 mA cm−2 current density at low overpotentials of 34 mV and exhibit a small Tafel slope of 31 mV dec−1 in acidic electrolytes of 0.5 M H2SO4, which is close to that of commercial Pt/C (20 wt%) electrocatalytic catalysts. In 1 M KOH solution, the PtNi/CNFs also exhibit excellent HER activity with a low overpotential of 82 mV to achieve a current density of 10 mA cm−2 and a small Tafel slope of 34 mV dec−1. Moreover, the PtNi/CNFs also show good activity for OER in alkaline electrolyte of 1 M KOH with a Tafel slope of 159 mV dec−1 and a small overpotential of 151 mV to reach a current density of 10 mA cm−2. In addition, the OER performance of the PtNi/CNFs in acid media is also favorable, with a 198 mV dec−1 Tafel slope. The decent activity of the PtNi/CNFs for water splitting originates from the synergistic effects of using Pt and Ni, large amounts of ultra-small nanoparticles densely dispersed on the CNFs, high conductivity of the support materials and interconnected three-dimensional structures of the carbon nanofiber mats.

Ni-Fe-P Nanoparticles Encapsulated in Carbon Nanotubes Supported on Carbon Cloth for Overall Water Splitting

Boosting Electrocatalytic Activities of Pt-Based Mesoporous Nanoparticles for Overall Water Splitting by a Facile Ni, P Co-Incorporation Strategy

Co–Ni‐Based Nanotubes/Nanosheets As Efficient Water Splitting Electrocatalysts

N, P co-doped Ni/Mo-based multicomponent electrocatalysts in situ decorated on Ni foam for overall water splitting

Partially Oxidized Ni Nanoparticles Supported on Ni-N Co-Doped Carbon Nanofibers As Bifunctional Electrocatalysts for Overall Water Splitting

FeNi3-Fe3O4 heterogeneous nanoparticles anchored on 2D MOF nanosheets/1D CNTs matrix as highly efficient bifunctional electrocatalyst for water splitting

Single-Atom and Bimetallic Nanoalloy Supported on Nanotubes As a Bifunctional Electrocatalyst for Ultrahigh-Current-Density Overall Water Splitting

A Bifunctional Electrocatalyst of PtNi Nanoparticles Immobilized on Three-Dimensional Carbon Nanofiber Mats for Efficient and Stable Water Splitting in Both Acid and Basic Media

Self-supporting Amorphous Nanoporous NiFeCoP Electrocatalyst for Efficient Overall Water Splitting

Nickel promoted cobalt disulfide nanowire array supported on carbon cloth: An efficient and stable bifunctional electrocatalyst for full water splitting

Nickel iron phosphide ultrathin nanosheets anchored on nitrogen-doped carbon nanoflake arrays as a bifunctional catalyst for efficient overall water splitting

NiCoP Nanopeapods Embedded in Carbon Nanotube Arrays As Bifunctional Catalysts for Efficient Overall Water Splitting

Immobilization of Ni3Co Nanoparticles into N‐Doped Carbon Nanotube/Nanofiber Integrated Hierarchically Branched Architectures Toward Efficient Overall Water Splitting

Self-Supported FeNi-P Nanosheets with Thin Amorphous Layers for Efficient Electrocatalytic Water Splitting

Self-supporting NiMo-Fe-P Nanowire Arrays As Bifunctional Catalysts for Efficient Overall Water Splitting.

Synergistic Coupling of Ni Nanoparticles with Ni3 C Nanosheets for Highly Efficient Overall Water Splitting

Fe2P Encapsulated in Carbon Nanowalls Decorated with Well-Dispersed Fe3C Nanodots for Efficient Hydrogen Evolution and Oxygen Reduction Reactions.

A Freestanding Single-Wall Carbon Nanotube Film Decorated with N-Doped Carbon-Encapsulated Ni Nanoparticles as a Bifunctional Electrocatalyst for Overall Water Splitting

RuNi Nanoparticles Embedded in N‐Doped Carbon Nanofibers As a Robust Bifunctional Catalyst for Efficient Overall Water Splitting

Ni Strongly Coupled with Mo2C Encapsulated in Nitrogen‐Doped Carbon Nanofibers As Robust Bifunctional Catalyst for Overall Water Splitting

Bifunctional Iron–Nickel Nitride Nanoparticles As Flexible and Robust Electrode for Overall Water Splitting