Abstract:N-doped porous carbon (N-PC) is considered as a promising candidate for electrochemical energy storage. However, the complicated multistep process is the biggest bottleneck. Here, a facile one-step strategy was employed to fabricate the N-doped porous carbon via the co-pyrolysis of urea and poly(acrylic acid- co -maleic acid) sodium salt (PAMS) without the protection of inert gas at 550 °C. When the mass ratio of urea to PAMS is 4:1, the microstructure and electrochemical properties of the as-prepared sample (N-4PC) are obviously improved compared with that of the direct carbonization of PAMS (PC). N-4PC presents salient peculiarities with much more mesopores, higher specific surface area of 181.5 m 2 g −1 far more than PC (23.6 m 2 g −1 ), and its nitrogen content is up to 10.61 at. %. In a three-electrode configuration using 6 M KOH, owing to the synergistic effect of pyridinic N, pyrrolic N and graphitic N atoms, N-4PC shows an outstanding specific capacity of 210 F g −1 far more than that of PC (93 F g −1 ) at 1 A g −1 , and a significant capacity retention rate of 79 % much higher than PC (47 %) at 20 A g −1 . Furthermore, the symmetric supercapacitor fabricated by N-4PC delivers an attractive specific capacitance of 140 F g −1 at 1 A g −1 , and 4.9 Wh kg −1 energy density when the power density is 265 W kg −1 in 6 M KOH. The equipment achieves superior cycle stability with capacity retention of 97 % after 7000 cycles at 1 A g −1 . Additionally, N-4PC also achieves great energy densities of 6.7 Wh kg −1 at the power density of 372.3 W kg −1 in 1 M H 2 SO 4 and 12.5 Wh kg −1 at the power density of 521.5 W kg −1 in 1 M Li 2 SO 4 . The fabricated nitrogen-doped porous carbon material has a great potential application prospect in energy storage equipment.

One-step Fabrication of N/O Self-Doped Porous Carbon Derived from 2-Meim for High-Performance Supercapacitor Electrode

Highly Active N, O-doped Hierarchical Porous Carbons for High-Energy Supercapacitors

Highly N/O co-doped ultramicroporous carbons derived from nonporous metal-organic framework for high performance supercapacitors

Preparation of N/O co-doped porous carbon by a one-step activation method for supercapacitor electrode materials

One-step Carbonization of Poly(styrene/divinylbenzene) to Fabricate N-doped Porous Carbon for High-Performance Supercapacitor Electrode

Biotemplating Preparation of N,O-codoped Hierarchically Porous Carbon for High-Performance Supercapacitors

Porous Carbon Electrode from Starch Soluble for Realizing High‐Performance Supercapacitor

High Performance Supercapacitors Electrode Based on N-Doped Carbon Nanofibers

Dual-template endowing N, O co-doped hierarchically porous carbon from potassium citrate with high capacitance and rate capability for supercapacitors

N/O Co-doped Porous Carbon with Controllable Porosity Synthesized via an All-in-One Step Method for a High-Rate-Performance Supercapacitor

Fabrication of high performance structural N-doped hierarchical porous carbon for supercapacitors

One-step Production of O-N-S Co-Doped Three-Dimensional Hierarchical Porous Carbons for High-Performance Supercapacitors

Nitrogen source-mediated cocoon silk-derived N, O-doped porous carbons for high performance symmetric supercapacitor

Fabrication of nitrogen and phosphorus-codoped porous carbon for high volumetric performance supercapacitors

Porous N Self-Doped Carbon Materials for High-Performance Supercapacitors Via Nanosized Silica Template Combined with Pyrolysis Method

One-step synthesis of polymer based N-doped porous carbon with enriched nitrogen content and its enhanced electrochemical properties in supercapacitors

O-N-S self-doped porous fusiform carbon particles derived from hair for high-performance supercapacitors

Fabrication of N/O self-doped hierarchical porous carbons derived from modified coal tar pitch for high-performance supercapacitors

Chitosan-Based Synthesis of O, N, and P Codoped Hierarchical Porous Carbon as Electrode Materials for Supercapacitors

N-doped layered porous carbon electrodes with high mass loadings for high-performance supercapacitors

Facile synthesis of N/P co-doped carbons with tailored hierarchically porous structures for supercapacitor applications