Abstract:The residual crack defects on the surface of potassium dihydrogen phosphate (KDP) crystals are the bottleneck that limits the improvement of laser damage resistance in the application of high-power laser devices. The multiple stress waves introduced by these residual surface lateral cracks on crystals under laser irradiation are the main inducement for damage extension and reduction of laser damage resistance. However, the coupling of these stress waves complicates their propagation in the crystal, and the interaction mechanism between each stress wave and laser damage has not been quantitatively characterized. Herein, a laser damage dynamic model for surface lateral cracks is constructed to reproduce the dynamic behaviors of the evolution of micro-defects to sub-millimeter damage pits under laser irradiation. Combined with the time-resolved pump and probe technique, the distribution of stress waves induced by lateral cracks was detected in situ to determine the type of stress waves. Then, the initiation and extension of laser damage were analyzed quantitatively to establish the correlations between different stress waves and damage extension. It is found that the longitudinal, shear, and Rayleigh waves induced by lateral cracks lead to large crush zones on the surface of KDP crystals, as well as butterfly-like damage sites accompanied by a large number of cracks at the bottom in the longitudinal section. The scale of the damage site can reach up to approximately 150 µm for lateral crack defects with large surface widths. This study ultimately reveals the physical mechanism of damage evolution induced by lateral cracks, providing effective guidance for developing control standards of surface crack defects during optical ultra-precision machining processes. This is of great significance for the improvement of laser damage resistance of KDP crystals in high-power laser systems.

Concentration Characterization of Underlying Intrinsic Defects Accompany with Surface Structural Defects and Their Effect on Laser Damage Resistance

Determination of Intrinsic Defects of Functional KDP Crystals with Flawed Surfaces and Their Effect on the Optical Properties

Determination of Stress Waves and Their Effect on the Damage Extension Induced by Surface Defects of KDP Crystals under Intense Laser Irradiation

Laser damage evolution by defects on diamond fly-cutting KDP surfaces

Initial energy deposition and initiation mechanism of nanosecond laser damage caused by KDP surface micro-defects

Influence of Surface Cracks on Laser-Induced Damage Resistance of Brittle Kh2po4 Crystal

Study of Modulation Property to Incident Laser by Surface Micro-Defects on KH 2 PO 4 Crystal

Recent Advances in Laser-Induced Surface Damage of KH2PO4 Crystal

Combining laser-induced fluorescence and light-scattering microscopies to diagnose low-fluence damage precursors on KDP-based crystal surface

Evolution of the Point Defects Involved under the Action of Mechanical Forces on Mechanically Machined Fused Silica Surfaces

Surface damage evolution of KDP crystals induced by conical cracks under irradiation of nanosecond laser

Relationship Between the Photoluminescence Envelope Area of Surface Defects and the Laser-Induced Damage Thresholds of Mechanically Machined Fused Silica Optical Surfaces

Study of Morphological Feature and Mechanism of Potassium Dihydrogen Phosphate Surface Damage under a 351 Nm Nanosecond Laser.

Influence of Cr3+ Cluster Defects on Crystal Structure and Optical Properties of KDP Crystals Studied by DFT and UV-Vis

Study on incident laser modulation using surface micro-defects on KH_2PO_4 crystal

Characterization of manufacturing-induced surface scratches and their effect on laser damage resistance performance of diamond fly-cut KDP crystal

Influence of Light Intensification by Subsurface Cracks on KH2PO4 Crystal's Laser Induced Damage Threshold

Laser Induced Damage Of Potassium Dihydrogen Phosphate (Kdp) Optical Crystal Machined By Water Dissolution Ultra-Precision Polishing Method

The decisive effects of the stress states and brittle-plasticity of the surface defects on their laser-induced damage thresholds on fused silica surfaces

On the Ultra-Precision Fabrication of Damage-Free Optical KDP Components: Mechanisms and Problems

Structural and electronic properties and optical absorption of oxygen vacancy cluster defects in KDP crystals: hybrid density functional theory investigation