Enhancement of M-Cresol Hydrodeoxygenation Selectivity on Ni Catalysts by Surface Decoration of MoOx Species
Feifei Yang,Nicole J. Libretto,Mallikharjuna Rao Komarneni,Wei Zhou,Jeffrey T. Miller,Xinli Zhu,Daniel E. Resasco
DOI: https://doi.org/10.1021/acscatal.9b01285
IF: 12.9
2019-01-01
ACS Catalysis
Abstract:Catalysts based on earth-abundant elements, such as Ni and Mo, that can be used for the conversion of lignin-derived compounds are desirable. However, they usually exhibit low activity and/or selectivity toward the target reaction, hydrodeoxygenation (HDO). For example, conversion of m-cresol in H-2 over a typical Ni/SiO2 leads to ring hydrogenation at low temperatures and C-C hydrogenolysis to CH4 at high temperatures. Here, we report that a bimetallic Ni-Mo/SiO2 catalyst with Ni:Mo ratio approximate to 1 reduced at an optimized temperature can be very active and selective for HDO of m-cresol to toluene over a wide range of reaction temperatures (250-350 degrees C) and 1 atm of H-2. This behavior is explained in terms of the surface structure of Mo oxides on the surface of Ni nanoparticles. Detailed characterization (XRD, Raman, TPR, EXAFS, and XPS) indicates that, after calcination, NiMoO4 is the predominant phase. However, after subsequent reduction, metallic Ni nanoparticles segregate out of the partially reduced MoOx. Interestingly, while no significant structural/electronic modifications are detected for the bulk of the metallic Ni particles, the surface chemistry is clearly altered (i.e., no hydrogenolysis/hydrogenation, weak CO/H-2 adsorption, and lower electron density in the d band of Ni). These results suggest that after reduction, in contrast to the formation of NiMo alloy, the Ni surface gets decorated by reduced MoOx moieties, a phenomenon similar to that previously observed on reducible oxides (so-called SMSI), which is essential for maximizing HDO and inhibiting hydrogenolysis.