Shunt Mitigation Toward Efficient Large-Area Perovskite-Silicon Tandem Solar Cells

Guang Yang,Zhengshan J. Yu,Mengru Wang,Zhifang Shi,Zhenyi Ni,Haoyang Jiao,Chengbin Fei,Allen Wood,Abdulwahab Alasfour,Bo Chen,Zachary C. Holman,Jinsong Huang
DOI: https://doi.org/10.1016/j.xcrp.2023.101628
IF: 8.9
2023-01-01
Cell Reports Physical Science
Abstract:The efficiency of small-area perovskite-silicon tandem solar cells is already above 30%; however, there are few studies about large -area tandem cells. One main challenge for the upscaling of perovskite-silicon tandems is the non-uniformity of perovskites across large areas of tandem cells that can cause shunting, which becomes more serious when large-area tandems are fabricated via a solution process. Here, we demonstrate the fabrication of efficient large -area tandems on industry-compatible Czochralski-grown and chemically etched rough silicon wafers using a blading process. We employed a lithium fluoride (LiF) interlayer to significantly mitigate the shunting issue for large-area tandems when it is deposited on the hole transport layer side. The LiF interlayer decreases local current drains and improves interfacial contact at the buried perovskite interface. As a result, a stabilized power conversion efficiency of 25.1% is achieved for tandem devices with a large aperture area of 24 cm2.
What problem does this paper attempt to address?