Construction of the POMOF@Polypyrrole Composite with Enhanced Ion Diffusion and Capacitive Contribution for High-Performance Lithium-Ion Batteries
Zhiyuan Han,Xueying Li,Qiang Li,Hongsen Li,Jie Xu,Na Li,Guoxia Zhao,Xia Wang,Hongliang Li,Shandong Li
DOI: https://doi.org/10.1021/acsami.0c20721
2021-01-27
Abstract:Polyoxometalate (POM) as an "electronic sponge" can store a great number of electrons; however, shortcomings of poor conductivity and solubility in electrolytes cause a significant decrease in specific capacity and poor rate capability. To address the aforementioned disadvantages, a dual strategy was proposed, including coating the conductive polypyrrole (PPy) and utilizing nitrogenous ligands (1,10-phenanthroline monohydrate = 1,10-phen) for metal–organic frameworks (MOFs) to fabricate a [Cu(1,10-phen)(H<sub>2</sub>O)<sub>2</sub>]<sub>2</sub>[Mo<sub>6</sub>O<sub>20</sub>]@PPy () composite, effectively confining the POM in MOFs to avoid dissolution of POM in the electrolyte and improve electrochemical stability. Simultaneously, the PPy shell could improve the conductivity, contribute extra capacity, and alleviate volume variation of Cu-POMOF during cycling. Therefore, the final composite provides an excellent specific capacity of around 769 mA h g<sup>–1</sup> at 0.1 A g<sup>–1</sup> after 160 cycles and good rate performance, associated with great cycling stability (319 mA h g<sup>–1</sup> at 2 A g<sup>–1</sup> after 500 cycles). Moreover, the electrochemical reaction mechanism of was investigated by <i>ex situ</i> XPS measurements, indicating that storage of electrons results from the reduction/oxidation of Mo atoms (Mo<sup>6+</sup> ↔ Mo<sup>4+</sup>) and Cu atoms (Cu<sup>2+</sup> ↔ Cu<sup>0</sup>). As a consequence, this work not only proposes a novel method for preparing POM-based lithium-ion batteries but also expands the variety of anode materials.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsami.0c20721?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsami.0c20721</a>.Raman spectra of Cu-POMOF, PPy, and ; N<sub>2</sub> adsorption–desorption isotherms of ; higher magnification TEM of ; TGA curves of Cu-POMOF and ; EDS spectrum and element content of ; high-resolution XPS spectra of Cu 2p; cycling properties at 2 A g<sup>–1</sup> of and Cu-POMOF-2; cycling properties at 1 A g<sup>–1</sup> of PPy; SEM image of and Cu-POMOF after 100 cycles; TEM image of the after 100 cycles; CV curves of Cu-POMOF at 0.2 mV s<sup>–1</sup>; and comparison of and other POMOF-based anodes in this work and other literature (<a class="ext-link" href="/doi/suppl/10.1021/acsami.0c20721/suppl_file/am0c20721_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.
materials science, multidisciplinary,nanoscience & nanotechnology