Facile Synthesis of Ni/sepiolite and Its Excellent Performance Toward Electrocatalytic Ethanol Oxidation

Liang Li,Junkai Zhao,Yu Sun,Xinming Yang,Jianjun Chen

DOI: https://doi.org/10.1007/s10800-023-01990-0

IF: 2.925

2024-01-01

Journal of Applied Electrochemistry

Abstract:Effective and stable catalysts toward ethanol oxidation reaction (EOR) is very important for the application of direct ethanol fuel cells (DEFCs). This research reports a facile synthesis of Ni/sepiolite (Ni/SEP) catalyst through incipient wetness impregnation method, which has large amount of active sites and excellent electrochemical activity toward EOR. Through scanning electron microscope with energy dispersive spectroscopy (SEM-EDS), nickel was found to distribute evenly on the fiber structure of sepiolite through ion exchange with the element magnesium without altering the main structure. With a geometric surface area of 0.07 cm2, Ni/SEP had a larger electrochemical surface area 0.44 m2 g−1, lower onset potential of 0.28 V (vs. SCE), higher peak current density (258.5 mA cm−2), and smaller Tafel slope (20 mV dec−1), indicating a superior electrochemical activity toward EOR. Within the experimental conditions, it was observed to be a diffusion-controlled process based on the linear relationship between peak current and root of scan rates, and the reaction could be accelerated by the increase of both C2H5OH and KOH concentrations. Through the study of cyclic voltammetry as well as calculation of apparent activation energy, an electrolytic-chemical (EC) reaction mechanism was suggested with high valence Ni species as the electron transfer carrier.